Durethan® AKV50H2.0
50% 玻纤增强, 注塑成型, 热稳定
通用信息
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
特殊性能
- 热稳定性或耐热性
法规
- Absence Declaration BNST2023-11-16
- Absence Declaration Biocidal Products2025-11-21
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals and F-gasses2025-02-06
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2025-04-14
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration PFAS2025-01-31
- Absence Declaration POPs (Persistent Organic Pollutants)2025-10-21
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Compliance Statement Sanctions and Embargos2025-11-24
- Conflict minerals declaration (EICC, GeSI)2025-10-21
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2025-11-03
- EMRT Statement2025-05-27
- Micro Plastics Statement2025-09-22
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- Packaging, Packaging Waste (EU) 2025/40 and CONEG declaration2025-06-24
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2025-11-06
加工工艺
注塑成型
注塑成型
汽车OEM
CALLOUT, GM
CALLOUT, GM
OEM规格
ASTM D6779 PA012G50
GMW3038
ASTM D6779 PA012G50
GMW3038
流变性能
成型收缩率(平行)
0.35
%
ISO 294-4
成型收缩率(垂直)
0.9
%
ISO 294-4
机械性能
拉伸模量
16000
MPa
ISO 527-1/-2
拉伸模量 (-40°C)
16500
MPa
ISO 527-1/-2
拉伸模量 (40°C)
15000
MPa
ISO 527-1/-2
拉伸模量 (100°C)
8000
MPa
ISO 527-1/-2
拉伸模量 (120°C)
7400
MPa
ISO 527-1/-2
拉伸模量 (140°C)
6900
MPa
ISO 527-1/-2
拉伸模量 (150°C)
6600
MPa
ISO 527-1/-2
拉伸模量 (160°C)
6300
MPa
ISO 527-1/-2
拉伸模量 (180°C)
5700
MPa
ISO 527-1/-2
拉伸模量 (200°C)
5200
MPa
ISO 527-1/-2
拉伸模量 (210°C)
4900
MPa
ISO 527-1/-2
断裂应力
235
MPa
ISO 527-1/-2
断裂应力（-40°C)
300
MPa
ISO 527-1/-2
断裂应力（100°C)
135
MPa
ISO 527-1/-2
断裂应力（120°C)
120
MPa
ISO 527-1/-2
断裂应力(140°C)
110
MPa
ISO 527-1/-2
断裂应力(150°C)
105
MPa
ISO 527-1/-2
断裂应力(160°C)
100
MPa
ISO 527-1/-2
拉伸应力 (180°C)
85
MPa
ISO 527-1/-2
拉伸应力 (200°C)
75
MPa
ISO 527-1/-2
断裂应力 (210°C)
70
MPa
ISO 527-1/-2
断裂伸长率
2.7
%
ISO 527-1/-2
断裂应变(-40°C)
2.6
%
ISO 527-1/-2
断裂应变(120°C)
5.1
%
ISO 527-1/-2
断裂应变 (140°C)
5.3
%
ISO 527-1/-2
断裂应变 (150°C)
5.4
%
ISO 527-1/-2
断裂应变(160°C)
5.5
%
ISO 527-1/-2
断裂应变(180°C)
5.7
%
ISO 527-1/-2
断裂应变(200°C)
5.9
%
ISO 527-1/-2
断裂应变 (210°C)
6
%
ISO 527-1/-2
弯曲模量
15500
MPa
ISO 178
弯曲模量 (120°C)
8000
MPa
ISO 178
弯曲模量 (160°C)
7000
MPa
ISO 178
弯曲模量 (180°C)
6500
MPa
ISO 178
弯曲模量 (200°C)
6100
MPa
ISO 178
弯曲模量(210°C)
5800
MPa
ISO 178
弯曲强度
355
MPa
ISO 178
弯曲强度 (120°C)
175
MPa
ISO 178
弯曲强度 (160°C)
140
MPa
ISO 178
弯曲强度 (180°C)
128
MPa
ISO 178
弯曲强度 (200°C)
115
MPa
ISO 178
弯曲强度 (210°C)
110
MPa
ISO 178
简支梁无缺口冲击强度(+23°C)
95
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(-30°C)
100
kJ/m²
ISO 179/1eU
简支梁缺口冲击强度(+23°C)
16
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(-30°C)
14
kJ/m²
ISO 179/1eA
悬臂梁缺口冲击强度(23°C)
15
kJ/m²
ISO 180/1A
最大刺穿力(+23°C)
1100
N
ISO 6603-2
最大刺穿力（-30°C)
1000
N
ISO 6603-2
刺穿能(+23°C)
4
J
ISO 6603-2
刺穿能（-30°C)
3
J
ISO 6603-2
熔接痕强度 （厚度1）
95
MPa
ISO 527-1/-2
热性能
熔融温度(10°C/min)
261
°C
ISO 11357-1/-3
热变形温度(1.80 MPa)
247
°C
ISO 75-1/-2
热变形温度(0.45 MPa)
250
°C
ISO 75-1/-2
线热膨胀系数(平行)
0.2
E-4/°C
ISO 11359-1/-2
线热膨胀系数(垂直)
0.8
E-4/°C
ISO 11359-1/-2
厚度为h时的燃烧性
HB
class
IEC 60695-11-10
测试厚度
0.75
mm
IEC 60695-11-10
燃烧性（1.5mm厚度）
HB
class
IEC 60695-11-10
测试厚度
1.5
mm
IEC 60695-11-10
UL认证
Yes
-
-
厚度为h时的燃烧性
HB
class
IEC 60695-11-10
测试用试样的厚度
3
mm
IEC 60695-11-10
UL认证
Yes
-
-
燃烧性－氧指数
27
%
ISO 4589-1/-2
球压温度
258
°C
IEC 60695-10-2
灼热丝燃烧指数GWFI
600
°C
IEC 60695-2-12
GWFI (厚度(1))
2
mm
IEC 60695-2-12
相对温度指数-电气
120
°C
UL746B
相对温度指数-电气（厚度1）
0.75
mm
UL746B
相对温度指数-冲击
95
°C
UL746B
相对温度指数-冲击（厚度1）
0.75
mm
UL746B
相对温度指数-冲击
105
°C
UL746B
相对温度指数-冲击（厚度2）
1.5
mm
UL746B
相对温度指数-非冲击
115
°C
UL746B
相对温度指数-非冲击（厚度1）
0.75
mm
UL746B
相对温度指数-非冲击
120
°C
UL746B
相对温度指数-非冲击（厚度2）
1.5
mm
UL746B
电性能
相对介电常数(100Hz)
4.5
-
IEC 62631-2-1
相对介电常数(1MHz)
4
-
IEC 62631-2-1
介质损耗因子(100Hz)
90
E-4
IEC 62631-2-1
介质损耗因子(1MHz)
150
E-4
IEC 62631-2-1
体积电阻率
1E13
Ohm*m
IEC 62631-3-1
表面电阻率
Ohm
IEC 62631-3-2
介电强度
40
kV/mm
IEC 60243-1
相对漏电起痕指数
550
V
IEC 60112
其它性能
吸水率
4
%
Sim. to ISO 62
吸湿率
1.2
%
Sim. to ISO 62
密度
1570
kg/m³
ISO 1183
材料特性
粘数
146
cm³/g
ISO 307, 1157, 1628
空气干燥机干燥温度
80
°C
空气干燥机干燥温度
2-6
h
残余水分含量
0.03-0.12
%
acc. to Karl Fischer
熔体温度(Tmin - Tmax)
280-300
°C
模具温度
80-120
°C