Durethan® BKV50HEF DUS022
50%유리섬유강화, 사출 성형, 열안정, 높은 흐름성
일반 정보
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
특징
- Good or high flow
- Heat stabilized
각종규제
- Absence Declaration BNST2023-11-16
- Absence Declaration Biocidal Products2025-11-21
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals and F-gasses2025-02-06
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2025-04-14
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration PFAS2025-01-31
- Absence Declaration POPs (Persistent Organic Pollutants)2025-10-21
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Compliance Statement Sanctions and Embargos2025-11-24
- Conflict minerals declaration (EICC, GeSI)2025-10-21
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2025-11-03
- EMRT Statement2025-05-27
- Micro Plastics Statement2025-09-22
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- Packaging, Packaging Waste (EU) 2025/40 and CONEG declaration2025-06-24
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2025-11-06
성형 기술
사출성형
사출성형
자동차 OEM
GM
GM
OEM 규격
GMW15702
GMW15702
유변학적 특성
성형 수축률. 평행
0.2
%
ISO 294-4
성형 수축률. 수직
0.7
%
ISO 294-4
기계적 특성
인장탄성률
16200
MPa
ISO 527-1/-2
인장탄성률 (-40°C)
17600
MPa
ISO 527-1/-2
인장탄성률 (40°C)
14900
MPa
ISO 527-1/-2
인장탄성률 (100°C)
7110
MPa
ISO 527-1/-2
인장탄성률 (120°C)
6570
MPa
ISO 527-1/-2
인장탄성률 (140°C)
6190
MPa
ISO 527-1/-2
인장탄성률 (160°C)
5860
MPa
ISO 527-1/-2
인장탄성율 (180°C)
5330
MPa
ISO 527-1/-2
인장탄성율 (200°C)
4580
MPa
ISO 527-1/-2
파단시 강도
205
MPa
ISO 527-1/-2
파단시 신율
2.3
%
ISO 527-1/-2
굴곡탄성률
15000
MPa
ISO 178
굴곡강도
320
MPa
ISO 178
챠피 충격 강도 +23°C
85
kJ/m²
ISO 179/1eU
챠피 충격 강도 -30°C
80
kJ/m²
ISO 179/1eU
챠피 노치드 충격 강도 +23°C
13
kJ/m²
ISO 179/1eA
챠피 노치드 충격 강도 -30°C
10
kJ/m²
ISO 179/1eA
아이조드 노치드 충격강도 (23°C)
14
kJ/m²
ISO 180/1A
최대 관통힘 +23°C
1220
N
ISO 6603-2
관통 에너지 +23°C
3.6
J
ISO 6603-2
열적 특성
녹는점 (10 °C/MIN)
220
°C
ISO 11357-1/-3
하중하에서의 변형온도 (1.80 MPa)
207
°C
ISO 75-1/-2
하중하에서의 변형온도 (0.45 MPa)
215
°C
ISO 75-1/-2
선형 열팽창 계수, 평행
0.1
E-4/°C
ISO 11359-1/-2
선형 열팽창 계수, 수직
0.8
E-4/°C
ISO 11359-1/-2
기타 특성
밀도
1570
kg/m³
ISO 1183
물질의 비성질
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
270-290
°C
Mold temperature
80-120
°C