Durethan® BKV230 DUS008
30%유리섬유강화, 사출 성형, 충격강도 개선
일반 정보
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
특징
각종규제
- Absence Declaration BNST2023-11-16
- Absence Declaration Biocidal Products2025-11-21
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals and F-gasses2025-02-06
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2025-04-14
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2025-10-21
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Compliance Statement Sanctions and Embargos2025-11-24
- Conflict minerals declaration (EICC, GeSI)2025-10-21
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2025-11-03
- EMRT Statement2025-05-27
- Micro Plastics Statement2025-09-22
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- Packaging, Packaging Waste (EU) 2025/40 and CONEG declaration2025-06-24
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2025-11-06
Yellow Card
성형 기술
사출성형
사출성형
유변학적 특성
성형 수축률. 평행
0.3
%
ISO 294-4
성형 수축률. 수직
0.8
%
ISO 294-4
기계적 특성
인장탄성률
8500
MPa
ISO 527-1/-2
인장탄성률 (-40°C)
8850
MPa
ISO 527-1/-2
인장탄성률 (40°C)
7350
MPa
ISO 527-1/-2
인장탄성률 (100°C)
3560
MPa
ISO 527-1/-2
인장탄성률 (120°C)
3350
MPa
ISO 527-1/-2
인장탄성률 (140°C)
3200
MPa
ISO 527-1/-2
인장탄성률 (160°C)
3020
MPa
ISO 527-1/-2
인장탄성율 (180°C)
2800
MPa
ISO 527-1/-2
인장탄성율 (200°C)
2370
MPa
ISO 527-1/-2
파단시 강도
130
MPa
ISO 527-1/-2
파단시 신율
4.1
%
ISO 527-1/-2
굴곡탄성률
7400
MPa
ISO 178
굴곡강도
205
MPa
ISO 178
챠피 충격 강도 +23°C
85
kJ/m²
ISO 179/1eU
챠피 충격 강도 -30°C
95
kJ/m²
ISO 179/1eU
챠피 노치드 충격 강도 +23°C
20
kJ/m²
ISO 179/1eA
챠피 노치드 충격 강도 -30°C
13
kJ/m²
ISO 179/1eA
아이조드 노치드 충격강도 (23°C)
20
kJ/m²
ISO 180/1A
열적 특성
녹는점 (10 °C/MIN)
220
°C
ISO 11357-1/-3
하중하에서의 변형온도 (1.80 MPa)
198
°C
ISO 75-1/-2
하중하에서의 변형온도 (0.45 MPa)
218
°C
ISO 75-1/-2
두께 H인 제품의 난연성
HB
class
IEC 60695-11-10
난연성 (테스트 두께)
0.75
mm
IEC 60695-11-10
두께 H인 제품의 난연성
HB
class
IEC 60695-11-10
난연성 (테스트 두께)
3
mm
IEC 60695-11-10
평균두께에서의 난연성
Yes
-
-
기타 특성
밀도
1320
kg/m³
ISO 1183
물질의 비성질
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
260-290
°C
Mold temperature
80-100
°C