Durethan® AC30 DUS027
非強化, 射出成形, 熱安定, 耐衝撃性
一般情報
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
特徴
- Heat stabilized
各種規制
- Absence Declaration BNST2023-11-16
- Absence Declaration Biocidal Products2025-11-21
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals and F-gasses2025-02-06
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2025-04-14
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration PFAS2025-01-31
- Absence Declaration POPs (Persistent Organic Pollutants)2025-10-21
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- CALIFORNIA PROPOSITION 65 (NDS)2025-01-20
- CALIFORNIA PROPOSITION 65 (carbon black)2025-01-20
- Compliance Statement Sanctions and Embargos2025-11-24
- Conflict minerals declaration (EICC, GeSI)2025-10-21
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2025-11-03
- EMRT Statement2025-05-27
- Micro Plastics Statement2025-09-22
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- Packaging, Packaging Waste (EU) 2025/40 and CONEG declaration2025-06-24
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2025-11-06
Yellow Card
成形方法
Injection Molding
Injection Molding
流動特性
メルトボリュームフローレイト
27
cm³/10min
ISO 1133
温度
270
°C
ISO 1133
荷重
2.16
kg
ISO 1133
成形収縮率 (流れ方向）
1.3
%
ISO 294-4
成形収縮率 (垂直方向)
1.8
%
ISO 294-4
機械特性
引張弾性率
3000
MPa
ISO 527-1/-2
引張降伏強度
70
MPa
ISO 527-1/-2
引張降伏ひずみ
6.5
%
ISO 527-1/-2
引張破断呼びひずみ
20
%
ISO 527-1/-2
曲げ弾性率
2600
MPa
ISO 178
曲げ強度
100
MPa
ISO 178
シャルピー衝撃強さ (23℃)
N
kJ/m²
ISO 179/1eU
シャルピー衝撃強さ (-30℃)
N
kJ/m²
ISO 179/1eU
シャルピー衝撃強さ ノッチ付き (23℃)
kJ/m²
ISO 179/1eA
アイゾット衝撃強さ ノッチ付き (23℃)
kJ/m²
ISO 180/1A
熱的特性
融点 (10℃/min)
261
°C
ISO 11357-1/-3
荷重たわみ温度 (1.8MPa)
70
°C
ISO 75-1/-2
荷重たわみ温度 (0.45MPa)
195
°C
ISO 75-1/-2
線膨張係数 (流れ方向)
0.8
E-4/°C
ISO 11359-1/-2
線膨張係数 (垂直方向)
1.1
E-4/°C
ISO 11359-1/-2
厚さhでの燃焼性
HB
class
IEC 60695-11-10
試験片厚さ
0.75
mm
IEC 60695-11-10
1.5mm厚さでの燃焼性
HB
class
IEC 60695-11-10
追加試験片の厚さ (1.5)
1.5
mm
IEC 60695-11-10
UL認定
Yes
-
-
その他特性
密度
1110
kg/m³
ISO 1183
材料特性
乾燥温度
80
°C
ドライエアーでの乾燥時間
2-6
h
残留水分量
0.03-0.12
%
acc. to Karl Fischer
溶融温度 (Tmin - Tmax)
270-290
°C
金型温度
80-90
°C