Durethan® BM29XH2.0EF
30% Glass/Mineral Reinforced, Injection Molding, Heat Stabilized, Improved flow
General Information
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
- Good or high flow
- Heat stabilized
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-06-27
Processing technology
Injection Molding
Injection Molding
Rheological properties
Molding shrinkage (parallel)
0.45
%
ISO 294-4
Molding shrinkage (normal)
0.65
%
ISO 294-4
Mechanical properties
Tensile modulus
6500
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
7500
MPa
ISO 527-1/-2
Tensile modulus (40°C)
5540
MPa
ISO 527-1/-2
Tensile modulus (100°C)
2500
MPa
ISO 527-1/-2
Tensile modulus (120°C)
2420
MPa
ISO 527-1/-2
Tensile modulus (140°C)
2300
MPa
ISO 527-1/-2
Tensile modulus (160°C)
2140
MPa
ISO 527-1/-2
Tensile modulus (180°C)
1910
MPa
ISO 527-1/-2
Tensile modulus (200°C)
1610
MPa
ISO 527-1/-2
Stress at break
110
MPa
ISO 527-1/-2
Strain at break
3
%
ISO 527-1/-2
Flexural modulus
6400
MPa
ISO 178
Flexural strength
180
MPa
ISO 178
Charpy impact strength (+23°C)
35
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
30
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
<10
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
<10
kJ/m²
ISO 179/1eA
Izod notched impact strength (+23°C)
<10
kJ/m²
ISO 180/1A
Thermal properties
Melting temperature (10°C/min)
220
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
190
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
210
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.4
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
0.9
E-4/°C
ISO 11359-1/-2
Burning Behav. at 1.5 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Electrical properties
Comparative tracking index
425
V
IEC 60112
Other properties
Water absorption
7
%
Sim. to ISO 62
Humidity absorption
2.2
%
Sim. to ISO 62
Density
1360
kg/m³
ISO 1183
Material specific properties
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
270-290
°C
Mold temperature
80-100
°C