Durethan® BKV230 DUS008
30% Glass Reinforced, Injection Molding, Improved Impact
General Information
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Compliance Statement EU Sanctions and Embargos2024-05-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Injection Molding
Rheological properties
Molding shrinkage (parallel)
0.3
%
ISO 294-4
Molding shrinkage (normal)
0.8
%
ISO 294-4
Mechanical properties
Tensile modulus
8500
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
8850
MPa
ISO 527-1/-2
Tensile modulus (40°C)
7350
MPa
ISO 527-1/-2
Tensile modulus (100°C)
3560
MPa
ISO 527-1/-2
Tensile modulus (120°C)
3350
MPa
ISO 527-1/-2
Tensile modulus (140°C)
3200
MPa
ISO 527-1/-2
Tensile modulus (160°C)
3020
MPa
ISO 527-1/-2
Tensile modulus (180°C)
2800
MPa
ISO 527-1/-2
Tensile modulus (200°C)
2370
MPa
ISO 527-1/-2
Stress at break
130
MPa
ISO 527-1/-2
Strain at break
4.1
%
ISO 527-1/-2
Flexural modulus
7400
MPa
ISO 178
Flexural strength
205
MPa
ISO 178
Charpy impact strength (+23°C)
85
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
95
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
20
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
13
kJ/m²
ISO 179/1eA
Izod notched impact strength (+23°C)
20
kJ/m²
ISO 180/1A
Thermal properties
Melting temperature (10°C/min)
220
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
198
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
218
°C
ISO 75-1/-2
Burning Behav. at 0.75 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
0.75
mm
IEC 60695-11-10
Burning Behav. at 3.0 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
3
mm
IEC 60695-11-10
UL recognition
Yes
-
-
Other properties
Density
1320
kg/m³
ISO 1183
Material specific properties
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
260-290
°C
Mold temperature
80-100
°C