Durethan® AC30 DUS027

Unreinforced, Injection Molding, Heat Stabilized, Improved Impact

Back to results

General Information

Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
  • Heat stabilized
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • CALIFORNIA PROPOSITION 65 (NDS)2024-01-02
  • Compliance Statement EU Sanctions and Embargos2024-05-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Have a question? Contact us

Rheological properties

Melt volume-flow rate
27
cm³/10min
Temperature
270
°C
Load
2.16
kg
Molding shrinkage (parallel)
1.3
%
Molding shrinkage (normal)
1.8
%

Mechanical properties

Tensile modulus
3000
MPa
Yield stress
70
MPa
Yield strain
6.5
%
Nominal strain at break
20
%
Flexural modulus
2600
MPa
Flexural strength
100
MPa
Charpy impact strength (+23°C)
N
kJ/m²
Charpy impact strength (-30°C)
N
kJ/m²
Charpy notched impact strength (+23°C)
<10
kJ/m²
Charpy notched impact strength (-30°C)
<10
kJ/m²
Izod notched impact strength (+23°C)
<10
kJ/m²

Thermal properties

Melting temperature (10°C/min)
261
°C
Temp. of deflection under load (1.80 MPa)
70
°C
Temp. of deflection under load (0.45 MPa)
195
°C
Coeff. of linear therm. expansion (parallel)
0.8
E-4/°C
Coeff. of linear therm. expansion (normal)
1.1
E-4/°C
Burning Behav. at 0.75 mm nom. thickn.
HB
class
Thickness tested
0.75
mm
Burning Behav. at 1.5 mm nom. thickn.
HB
class
Thickness tested
1.5
mm
UL recognition
Yes
-

Other properties

Density
1110
kg/m³

Material specific properties

Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
Melt temperature (Tmin - Tmax)
270-290
°C
Mold temperature
80-90
°C
admissible residence time at Tmax
<10
min