Pocan® BF4232HR 901510

30% 玻纤增强, 注塑成型, 阻燃, 耐水解性

返回至结果

通用信息

Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
特殊性能
  • 耐水解性或强水解稳定性
下载
法规
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Conflict minerals declaration (EICC, GeSI)2024-03-21
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
黄卡
加工工艺
注塑成型
有问题？联系我们

流变性能

熔体体积流动速率
16
cm³/10min
温度
260
°C
负荷
2.16
kg
成型收缩率(平行)
0.4
%
成型收缩率(垂直)
1.1
%

机械性能

拉伸模量
9800
MPa
拉伸模量 (-40°C)
12200
MPa
拉伸模量 (40°C)
9640
MPa
拉伸模量 (100°C)
5240
MPa
拉伸模量 (120°C)
4330
MPa
拉伸模量 (140°C)
3340
MPa
拉伸模量 (160°C)
2820
MPa
拉伸模量 (180°C)
2420
MPa
拉伸模量 (200°C)
1960
MPa
断裂应力
120
MPa
断裂伸长率
2
%
弯曲模量
10000
MPa
弯曲强度
185
MPa
Flexural strain at flexural strength
2.3
%
简支梁无缺口冲击强度(+23°C)
40
kJ/m²
悬臂梁冲击强度 (+23°C)
35
kJ/m²

热性能

熔融温度(10°C/min)
225
°C
热变形温度(1.80 MPa)
195
°C
热变形温度(0.45 MPa)
215
°C
线热膨胀系数(平行)
0.3
E-4/°C
线热膨胀系数(垂直)
1
E-4/°C
燃烧性（1.5mm厚度）
V-0
class
测试厚度
1.5
mm
燃烧性－氧指数
36.4
%
球压温度
212
°C
灼热丝燃烧指数GWFI
960
°C
GWFI (厚度(1))
0.4
mm
灼热丝燃烧指数GWFI
960
°C
GWFI(厚度(2))
0.75
mm
灼热丝引燃温度GWIT
900
°C
GWIT (厚度(1))
0.4
mm
灼热丝引燃温度GWIT
850
°C
GWIT (厚度(2))
0.75
mm
灼热丝引燃温度GWIT
725
°C
GWIT (厚度(3))
1.5
mm
灼热丝引燃温度GWIT
725
°C
GWIT (厚度(4))
3
mm

电性能

介电强度
29.8
kV/mm
相对漏电起痕指数
225
V
相对漏电起痕常数（PLC）
3
class

其它性能

密度
1670
kg/m³

图表