Pocan® ECOB3233HR
30% 玻纤增强, 注塑成型, 耐水解性, 流动性改良, 回收料含量
通用信息
Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
特殊性能
- 含回料成分
- 良好或高流动性
- 耐水解性或强水解稳定性
法规
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- CALIFORNIA PROPOSITION 65 (INDUSTRIAL USE)2024-01-02
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
加工工艺
注塑成型
注塑成型
流变性能
熔体体积流动速率
15
cm³/10min
ISO 1133
温度
260
°C
ISO 1133
负荷
2.16
kg
ISO 1133
成型收缩率(平行)
0.3
%
ISO 294-4
成型收缩率(垂直)
1
%
ISO 294-4
机械性能
拉伸模量
9600
MPa
ISO 527-1/-2
拉伸模量 (-40°C)
9750
MPa
ISO 527-1/-2
拉伸模量 (40°C)
7180
MPa
ISO 527-1/-2
拉伸模量 (100°C)
3980
MPa
ISO 527-1/-2
拉伸模量 (120°C)
3540
MPa
ISO 527-1/-2
拉伸模量 (140°C)
3150
MPa
ISO 527-1/-2
拉伸模量 (160°C)
2840
MPa
ISO 527-1/-2
拉伸模量 (180°C)
2440
MPa
ISO 527-1/-2
拉伸模量 (200°C)
2010
MPa
ISO 527-1/-2
断裂应力
125
MPa
ISO 527-1/-2
断裂伸长率
2.9
%
ISO 527-1/-2
弯曲模量
9100
MPa
ISO 178
弯曲强度
200
MPa
ISO 178
弯曲强度对应的弯曲应变
3.2
%
ISO 178-A
简支梁无缺口冲击强度(+23°C)
65
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(-30°C)
55
kJ/m²
ISO 179/1eU
悬臂梁冲击强度 (+23°C)
55
kJ/m²
ISO 180/1U
Izod冲击强度(-30°C)
55
kJ/m²
ISO 180-1U
热性能
熔融温度(10°C/min)
225
°C
ISO 11357-1/-3
热变形温度(1.80 MPa)
205
°C
ISO 75-1/-2
热变形温度(0.45 MPa)
220
°C
ISO 75-1/-2
线热膨胀系数(平行)
0.3
E-4/°C
ISO 11359-1/-2
线热膨胀系数(垂直)
1.3
E-4/°C
ISO 11359-1/-2
厚度为h时的燃烧性
HB
class
IEC 60695-11-10
测试厚度
0.75
mm
IEC 60695-11-10
燃烧性（1.5mm厚度）
HB
class
IEC 60695-11-10
测试厚度
1.5
mm
IEC 60695-11-10
UL认证
Yes
-
-
厚度为h时的燃烧性
HB
class
IEC 60695-11-10
测试用试样的厚度
3
mm
IEC 60695-11-10
UL认证
Yes
-
-
球压温度
209
°C
IEC 60695-10-2
灼热丝燃烧指数GWFI
800
°C
IEC 60695-2-12
GWFI (厚度(1))
0.8
mm
IEC 60695-2-12
灼热丝燃烧指数GWFI
800
°C
IEC 60695-2-12
GWFI(厚度(2))
1.5
mm
IEC 60695-2-12
灼热丝引燃温度GWIT
825
°C
IEC 60695-2-13
GWIT (厚度(1))
0.8
mm
IEC 60695-2-13
灼热丝引燃温度GWIT
825
°C
IEC 60695-2-13
GWIT (厚度(2))
1.5
mm
IEC 60695-2-13
灼热丝引燃温度GWIT
825
°C
IEC 60695-2-13
GWIT (厚度(3))
3
mm
IEC 60695-2-13
相对温度指数-电气
150
°C
UL746B
相对温度指数-电气（厚度1）
0.75
mm
UL746B
相对温度指数-冲击
140
°C
UL746B
相对温度指数-冲击（厚度1）
0.75
mm
UL746B
相对温度指数-非冲击
150
°C
UL746B
相对温度指数-非冲击（厚度1）
0.75
mm
UL746B
电性能
体积电阻率
>1E13
Ohm*m
IEC 62631-3-1
表面电阻率
>1E15
Ohm
IEC 62631-3-2
介电强度
35
kV/mm
IEC 60243-1
相对漏电起痕指数
475
V
IEC 60112
相对漏电起痕常数（PLC）
1
class
UL 746A
其它性能
密度
1480
kg/m³
ISO 1183
材料特性
循环空气干燥机干燥温度
120
°C
循环空气干燥机干燥温度
4-8
h
残余水分含量
0.00-0.02
%
acc. to Karl Fischer
熔体温度(Tmin - Tmax)
250-270
°C
模具温度
80-100
°C