Pocan® B1205XHR
非增强, 注塑成型, 耐水解性
通用信息
Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
特殊性能
- 耐水解性或强水解稳定性
法规
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-09-12
- 2024-05-16
加工工艺
注塑成型
注塑成型
流变性能
熔体体积流动速率
60
cm³/10min
ISO 1133
温度
260
°C
ISO 1133
负荷
2.16
kg
ISO 1133
成型收缩率(平行)
2.2
%
ISO 294-4
成型收缩率(垂直)
2.2
%
ISO 294-4
机械性能
拉伸模量
2100
MPa
ISO 527-1/-2
屈服应力
50
MPa
ISO 527-1/-2
屈服伸长率
5
%
ISO 527-1/-2
名义断裂伸长率
15
%
ISO 527-1/-2
弯曲模量
2200
MPa
ISO 178
弯曲强度
75
MPa
ISO 178
Flexural strain at flexural strength
6.7
%
ISO 178-A
简支梁无缺口冲击强度(+23°C)
140
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(-30°C)
80
kJ/m²
ISO 179/1eU
悬臂梁冲击强度 (+23°C)
100
kJ/m²
ISO 180/1U
热性能
熔融温度(10°C/min)
225
°C
ISO 11357-1/-3
热变形温度(1.80 MPa)
60
°C
ISO 75-1/-2
热变形温度(0.45 MPa)
140
°C
ISO 75-1/-2
线热膨胀系数(平行)
1.3
E-4/°C
ISO 11359-1/-2
线热膨胀系数(垂直)
1.3
E-4/°C
ISO 11359-1/-2
厚度为h时的燃烧性
HB
class
IEC 60695-11-10
测试厚度
0.75
mm
IEC 60695-11-10
燃烧性（1.5mm厚度）
HB
class
IEC 60695-11-10
测试厚度
1.5
mm
IEC 60695-11-10
UL认证
Yes
-
-
厚度为h时的燃烧性
HB
class
IEC 60695-11-10
测试用试样的厚度
3
mm
IEC 60695-11-10
UL认证
Yes
-
-
相对温度指数-电气
130
°C
UL746B
相对温度指数-电气（厚度1）
0.75
mm
UL746B
相对温度指数-冲击
150
°C
UL746B
相对温度指数-冲击（厚度1）
0.75
mm
UL746B
相对温度指数-非冲击
140
°C
UL746B
相对温度指数-非冲击（厚度1）
0.75
mm
UL746B
电性能
相对漏电起痕指数
600
V
IEC 60112
相对漏电起痕常数（PLC）
0
class
UL 746A
其它性能
密度
1290
kg/m³
ISO 1183
材料特性
Drying temperature circulating air dryer
120
°C
Drying time circulating air dryer
4-8
h
Residual moisture content
0.00-0.02
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
250-270
°C
Mold temperature
80-100
°C
熔体体积流动速率
60
cm³/10min
ISO 1133
温度
260
°C
ISO 1133
负荷
2.16
kg
ISO 1133
成型收缩率(平行)
2.2
%
ISO 294-4
成型收缩率(垂直)
2.2
%
ISO 294-4