Pocan® AF4110
12% 玻纤增强, 注塑成型, 阻燃, 低翘曲
通用信息
Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
特殊性能
- 低翘曲
法规
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-09-12
- 2024-05-16
加工工艺
注塑成型
注塑成型
流变性能
熔体体积流动速率
35
cm³/10min
ISO 1133
温度
260
°C
ISO 1133
负荷
5
kg
ISO 1133
成型收缩率(平行)
0.9
%
ISO 294-4
成型收缩率(垂直)
0.8
%
ISO 294-4
机械性能
拉伸模量
5800
MPa
ISO 527-1/-2
拉伸模量 (-40°C)
5820
MPa
ISO 527-1/-2
拉伸模量 (40°C)
4350
MPa
ISO 527-1/-2
拉伸模量 (100°C)
2520
MPa
ISO 527-1/-2
拉伸模量 (120°C)
1390
MPa
ISO 527-1/-2
拉伸模量 (140°C)
1040
MPa
ISO 527-1/-2
拉伸模量 (160°C)
669
MPa
ISO 527-1/-2
拉伸模量 (180°C)
420
MPa
ISO 527-1/-2
断裂应力
85
MPa
ISO 527-1/-2
断裂伸长率
2.5
%
ISO 527-1/-2
弯曲模量
5500
MPa
ISO 178
弯曲强度
135
MPa
ISO 178
Flexural strain at flexural strength
2.8
%
ISO 178-A
简支梁无缺口冲击强度(+23°C)
35
kJ/m²
ISO 179/1eU
悬臂梁冲击强度 (+23°C)
30
kJ/m²
ISO 180/1U
热性能
熔融温度(10°C/min)
225
°C
ISO 11357-1/-3
热变形温度(1.80 MPa)
130
°C
ISO 75-1/-2
热变形温度(0.45 MPa)
204
°C
ISO 75-1/-2
厚度为h时的燃烧性
V-0
class
IEC 60695-11-10
测试厚度
0.75
mm
IEC 60695-11-10
燃烧性（1.5mm厚度）
V-0
class
IEC 60695-11-10
测试厚度
1.5
mm
IEC 60695-11-10
UL认证
Yes
-
-
厚度为h时的燃烧性
V-0
class
IEC 60695-11-10
测试用试样的厚度
3
mm
IEC 60695-11-10
UL认证
Yes
-
-
灼热丝燃烧指数GWFI
960
°C
IEC 60695-2-12
GWFI (厚度(1))
0.75
mm
IEC 60695-2-12
灼热丝燃烧指数GWFI
960
°C
IEC 60695-2-12
GWFI(厚度(2))
1.5
mm
IEC 60695-2-12
灼热丝引燃温度GWIT
725
°C
IEC 60695-2-13
GWIT (厚度(1))
0.75
mm
IEC 60695-2-13
灼热丝引燃温度GWIT
700
°C
IEC 60695-2-13
GWIT (厚度(2))
1.5
mm
IEC 60695-2-13
灼热丝引燃温度GWIT
700
°C
IEC 60695-2-13
GWIT (厚度(3))
3
mm
IEC 60695-2-13
相对温度指数-电气
155
°C
UL746B
相对温度指数-电气（厚度1）
0.75
mm
UL746B
相对温度指数-冲击
110
°C
UL746B
相对温度指数-冲击（厚度1）
0.75
mm
UL746B
相对温度指数-非冲击
150
°C
UL746B
相对温度指数-非冲击（厚度1）
3
mm
UL746B
电性能
相对漏电起痕指数
250
V
IEC 60112
相对漏电起痕常数（PLC）
2
class
UL 746A
其它性能
密度
1480
kg/m³
ISO 1183
材料特性
Drying temperature circulating air dryer
120
°C
Drying time circulating air dryer
4-8
h
Residual moisture content
0.00-0.02
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
240-260
°C
Mold temperature
80-100
°C
熔体体积流动速率
35
cm³/10min
ISO 1133
温度
260
°C
ISO 1133
负荷
5
kg
ISO 1133
成型收缩率(平行)
0.9
%
ISO 294-4
成型收缩率(垂直)
0.8
%
ISO 294-4