Novamid® ES110C

易注塑级别

返回至结果

通用信息

Novamid®是高质量的聚酰胺，这条特殊的生产线主要是为满足日本客户的要求而设立的。
Novamid®应用地域广，行业宽，种类多。从汽车到包装，Novamid®背后都有经验丰富的专家队伍进行支持。
特殊性能
下载
法规
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-04-25
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
  • Absence Declaration Red Phosphorus2023-11-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
黄卡
加工工艺
注塑成型
有问题？联系我们

流变性能

熔体体积流动速率
44
cm³/10min
温度
230
°C
负荷
2.16
kg
熔融指数MFI
50
g/10min
MFI测试温度
230
°C
MFI测试负荷
2.16
kg
成型收缩率(平行)
1.1
%
成型收缩率(垂直)
1.3
%

机械性能

拉伸模量
3300
MPa
屈服应力
84
MPa
名义断裂伸长率
18
%
弯曲模量
2800
MPa
弯曲强度
114
MPa
简支梁无缺口冲击强度(+23°C)
N
kJ/m²
简支梁缺口冲击强度(+23°C)
4.1
kJ/m²

热性能

熔融温度(10°C/min)
220
°C
热变形温度(1.80 MPa)
76
°C
热变形温度(0.45 MPa)
173
°C
燃烧性（1.5mm厚度）
V-2
class
测试厚度
1.5
mm
UL认证
Yes
-
厚度为h时的燃烧性
V-2
class
测试用试样的厚度
3
mm
UL认证
Yes
-
相对温度指数-电气
130
°C
相对温度指数-电气（厚度1）
0.81
mm
相对温度指数-电气
130
°C
相对温度指数-电气（厚度2）
3
mm
相对温度指数-冲击
65
°C
相对温度指数-冲击（厚度1）
0.81
mm
相对温度指数-冲击
75
°C
相对温度指数-冲击（厚度2）
3
mm
相对温度指数-非冲击
80
°C
相对温度指数-非冲击（厚度1）
0.81
mm
相对温度指数-非冲击
85
°C
相对温度指数-非冲击（厚度2）
3
mm

其它性能

吸湿率
2.8
%
密度
1130
kg/m³

材料特性

粘数
118
cm³/g

图表