Durethan® BKV30FN04
30% 玻纤增强, 注塑成型, 阻燃(无卤), 热稳定
通用信息
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
特殊性能
- 热稳定性或耐热性
法规
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration PFAS2024-03-05
- Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Compliance Statement EU Sanctions and Embargos2024-05-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-11-08
加工工艺
注塑成型
注塑成型
汽车OEM
CALLOUT
CALLOUT
OEM规格
ASTM D6779 PA0220 G30 A33270 FF0008
ASTM D6779 PA0220 G30 A33270 FF0008
流变性能
熔体体积流动速率
17
cm³/10min
ISO 1133
温度
260
°C
ISO 1133
负荷
5
kg
ISO 1133
成型收缩率(平行)
0.2
%
ISO 294-4
成型收缩率(垂直)
0.7
%
ISO 294-4
机械性能
拉伸模量
10300
MPa
ISO 527-1/-2
拉伸模量 (-40°C)
11100
MPa
ISO 527-1/-2
拉伸模量 (40°C)
9360
MPa
ISO 527-1/-2
拉伸模量 (100°C)
4750
MPa
ISO 527-1/-2
拉伸模量 (120°C)
4270
MPa
ISO 527-1/-2
拉伸模量 (140°C)
3960
MPa
ISO 527-1/-2
拉伸模量 (160°C)
3720
MPa
ISO 527-1/-2
拉伸模量 (180°C)
3310
MPa
ISO 527-1/-2
拉伸模量 (200°C)
2730
MPa
ISO 527-1/-2
断裂应力
130
MPa
ISO 527-1/-2
断裂伸长率
3
%
ISO 527-1/-2
弯曲模量
10200
MPa
ISO 178
弯曲强度
230
MPa
ISO 178
简支梁无缺口冲击强度(+23°C)
60
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(-30°C)
55
kJ/m²
ISO 179/1eU
简支梁缺口冲击强度(+23°C)
kJ/m²
ISO 179/1eA
悬臂梁缺口冲击强度(23°C)
kJ/m²
ISO 180/1A
热性能
熔融温度(10°C/min)
220
°C
ISO 11357-1/-3
热变形温度(1.80 MPa)
205
°C
ISO 75-1/-2
热变形温度(0.45 MPa)
219
°C
ISO 75-1/-2
线热膨胀系数(平行)
0.2
E-4/°C
ISO 11359-1/-2
线热膨胀系数(垂直)
0.8
E-4/°C
ISO 11359-1/-2
厚度为h时的燃烧性
V-0
class
IEC 60695-11-10
测试用试样的厚度
0.4
mm
IEC 60695-11-10
厚度为h时的燃烧性
V-0
class
IEC 60695-11-10
测试厚度
0.75
mm
IEC 60695-11-10
燃烧性（1.5mm厚度）
V-0
class
IEC 60695-11-10
测试厚度
1.5
mm
IEC 60695-11-10
UL认证
Yes
-
-
厚度为h时的燃烧性
V-0
class
IEC 60695-11-10
测试用试样的厚度
3
mm
IEC 60695-11-10
UL认证
Yes
-
-
厚度为h时的5V燃烧性
5VA
class
IEC 60695-11-20
测试用试样的厚度
1.5
mm
IEC 60695-11-20
UL认证
Yes
-
-
燃烧性－氧指数
32
%
ISO 4589-1/-2
球压温度
209
°C
IEC 60695-10-2
灼热丝燃烧指数GWFI
960
°C
IEC 60695-2-12
GWFI (厚度(1))
0.4
mm
IEC 60695-2-12
灼热丝燃烧指数GWFI
960
°C
IEC 60695-2-12
GWFI(厚度(2))
0.75
mm
IEC 60695-2-12
灼热丝引燃温度GWIT
775
°C
IEC 60695-2-13
GWIT (厚度(1))
0.4
mm
IEC 60695-2-13
灼热丝引燃温度GWIT
775
°C
IEC 60695-2-13
GWIT (厚度(2))
0.75
mm
IEC 60695-2-13
相对温度指数-电气
140
°C
UL746B
相对温度指数-电气（厚度1）
0.4
mm
UL746B
相对温度指数-冲击
105
°C
UL746B
相对温度指数-冲击（厚度1）
0.4
mm
UL746B
相对温度指数-冲击
115
°C
UL746B
相对温度指数-冲击（厚度2）
0.75
mm
UL746B
相对温度指数-非冲击
130
°C
UL746B
相对温度指数-非冲击（厚度1）
0.4
mm
UL746B
相对温度指数-非冲击
140
°C
UL746B
相对温度指数-非冲击（厚度2）
0.75
mm
UL746B
电性能
相对介电常数(100Hz)
4
-
IEC 62631-2-1
相对介电常数(1MHz)
3.6
-
IEC 62631-2-1
介质损耗因子(100Hz)
145
E-4
IEC 62631-2-1
介质损耗因子(1MHz)
155
E-4
IEC 62631-2-1
体积电阻率
>1E13
Ohm*m
IEC 62631-3-1
介电强度
40
kV/mm
IEC 60243-1
相对漏电起痕指数
600
V
IEC 60112
其它性能
吸水率
4.6
%
Sim. to ISO 62
吸湿率
1.5
%
Sim. to ISO 62
密度
1420
kg/m³
ISO 1183
材料特性
空气干燥机干燥温度
80
°C
空气干燥机干燥温度
2-6
h
残余水分含量
0.03-0.07
%
acc. to Karl Fischer
熔体温度(Tmin - Tmax)
250-280
°C
模具温度
70-90
°C