Durethan® DPAKV30HREF
30% 玻纤增强, 注塑成型, 热稳定, 耐水解性, 流动性改良
通用信息
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
特殊性能
- 良好或高流动性
- 热稳定性或耐热性
- 耐水解性或强水解稳定性
下载
法规
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-06-27
加工工艺
注塑成型
注塑成型
流变性能
成型收缩率(平行)
0.37
%
ISO 294-4
成型收缩率(垂直)
0.82
%
ISO 294-4
机械性能
拉伸模量
8200
MPa
ISO 527-1/-2
拉伸模量 (-40°C)
9830
MPa
ISO 527-1/-2
拉伸模量 (40°C)
8500
MPa
ISO 527-1/-2
拉伸模量 (100°C)
4460
MPa
ISO 527-1/-2
拉伸模量 (120°C)
4080
MPa
ISO 527-1/-2
拉伸模量 (140°C)
3860
MPa
ISO 527-1/-2
拉伸模量 (160°C)
3670
MPa
ISO 527-1/-2
拉伸模量 (180°C)
3500
MPa
ISO 527-1/-2
拉伸模量 (200°C)
3420
MPa
ISO 527-1/-2
断裂应力
150
MPa
ISO 527-1/-2
断裂伸长率
3.6
%
ISO 527-1/-2
弯曲模量
8100
MPa
ISO 178
弯曲强度
240
MPa
ISO 178
简支梁无缺口冲击强度(+23°C)
80
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(-30°C)
70
kJ/m²
ISO 179/1eU
简支梁缺口冲击强度(+23°C)
10
kJ/m²
ISO 179/1eA
悬臂梁缺口冲击强度(23°C)
10
kJ/m²
ISO 180/1A
最大刺穿力(+23°C)
774
N
ISO 6603-2
最大刺穿力（-30°C)
756
N
ISO 6603-2
刺穿能(+23°C)
2.7
J
ISO 6603-2
刺穿能（-30°C)
2.5
J
ISO 6603-2
热性能
熔融温度(10°C/min)
263
°C
ISO 11357-1/-3
热变形温度(1.80 MPa)
240
°C
ISO 75-1/-2
热变形温度(0.45 MPa)
250
°C
ISO 75-1/-2
其它性能
密度
1320
kg/m³
ISO 1183
材料特性
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
280-300
°C
Mold temperature
80-120
°C