Durethan® BKV315ZH2.0
15% 玻纤增强, 吹塑级别, 挤出, 热稳定, 耐冲击改性
通用信息
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
特殊性能
- 热稳定性或耐热性
下载
法规
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-06-27
加工工艺
吹塑, 挤出
吹塑, 挤出
流变性能
成型收缩率(平行)
0.9
%
ISO 294-4
成型收缩率(垂直)
0.6
%
ISO 294-4
机械性能
拉伸模量
5300
MPa
ISO 527-1/-2
拉伸模量 (-40°C)
5810
MPa
ISO 527-1/-2
拉伸模量 (40°C)
4160
MPa
ISO 527-1/-2
拉伸模量 (100°C)
1750
MPa
ISO 527-1/-2
拉伸模量 (120°C)
1630
MPa
ISO 527-1/-2
拉伸模量 (140°C)
1520
MPa
ISO 527-1/-2
拉伸模量 (160°C)
1440
MPa
ISO 527-1/-2
拉伸模量 (180°C)
1350
MPa
ISO 527-1/-2
拉伸模量 (200°C)
1180
MPa
ISO 527-1/-2
断裂应力
105
MPa
ISO 527-1/-2
断裂伸长率
5
%
ISO 527-1/-2
弯曲模量
4800
MPa
ISO 178
弯曲强度
165
MPa
ISO 178
简支梁无缺口冲击强度(+23°C)
80
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(-30°C)
85
kJ/m²
ISO 179/1eU
简支梁缺口冲击强度(+23°C)
15
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(-30°C)
kJ/m²
ISO 179/1eA
悬臂梁缺口冲击强度(23°C)
15
kJ/m²
ISO 180/1A
最大刺穿力(+23°C)
1200
N
ISO 6603-2
最大刺穿力（-30°C)
630
N
ISO 6603-2
刺穿能(+23°C)
4.9
J
ISO 6603-2
刺穿能（-30°C)
2.5
J
ISO 6603-2
热性能
熔融温度(10°C/min)
221
°C
ISO 11357-1/-3
热变形温度(1.80 MPa)
175
°C
ISO 75-1/-2
热变形温度(0.45 MPa)
210
°C
ISO 75-1/-2
热变形温度(8.00 MPa)
58
°C
ISO 75-1/-2
线热膨胀系数(平行)
0.4
E-4/°C
ISO 11359-1/-2
线热膨胀系数(垂直)
1.3
E-4/°C
ISO 11359-1/-2
燃烧性（1.5mm厚度）
HB
class
IEC 60695-11-10
测试厚度
1.5
mm
IEC 60695-11-10
电性能
相对漏电起痕指数
375
V
IEC 60112
其它性能
密度
1200
kg/m³
ISO 1183
材料特性
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.0-0.06
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
270-290
°C
Mold temperature
80-120
°C