Durethan® BKV15H3.0 DUS008
15% 玻纤增强, 注塑成型, 热稳定
通用信息
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
特殊性能
- 热稳定性或耐热性
下载
法规
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-06-27
加工工艺
注塑成型
注塑成型
机械性能
拉伸模量
6500
MPa
ISO 527-1/-2
拉伸模量 (-40°C)
6460
MPa
ISO 527-1/-2
拉伸模量 (40°C)
5510
MPa
ISO 527-1/-2
拉伸模量 (100°C)
2470
MPa
ISO 527-1/-2
拉伸模量 (120°C)
2330
MPa
ISO 527-1/-2
拉伸模量 (140°C)
2220
MPa
ISO 527-1/-2
拉伸模量 (160°C)
2100
MPa
ISO 527-1/-2
拉伸模量 (180°C)
1960
MPa
ISO 527-1/-2
拉伸模量 (200°C)
1810
MPa
ISO 527-1/-2
断裂应力
130
MPa
ISO 527-1/-2
断裂伸长率
3
%
ISO 527-1/-2
弯曲模量
5500
MPa
ISO 178
弯曲强度
205
MPa
ISO 178
简支梁无缺口冲击强度(+23°C)
50
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(-30°C)
45
kJ/m²
ISO 179/1eU
悬臂梁缺口冲击强度(23°C)
kJ/m²
ISO 180/1A
热性能
熔融温度(10°C/min)
220
°C
ISO 11357-1/-3
热变形温度(1.80 MPa)
195
°C
ISO 75-1/-2
热变形温度(0.45 MPa)
215
°C
ISO 75-1/-2
线热膨胀系数(平行)
0.3
E-4/°C
ISO 11359-1/-2
线热膨胀系数(垂直)
1
E-4/°C
ISO 11359-1/-2
其它性能
密度
1230
kg/m³
ISO 1183
材料特性
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
260-290
°C
Mold temperature
80-100
°C