Durethan® BKV15H2.0 901510
15% 玻纤增强, 注塑成型, 热稳定
通用信息
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
特殊性能
- 热稳定性或耐热性
下载
法规
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-03-27
加工工艺
注塑成型
注塑成型
机械性能
拉伸模量
6000
MPa
ISO 527-1/-2
拉伸模量 (-40°C)
6140
MPa
ISO 527-1/-2
拉伸模量 (40°C)
4960
MPa
ISO 527-1/-2
拉伸模量 (100°C)
2180
MPa
ISO 527-1/-2
拉伸模量 (120°C)
2060
MPa
ISO 527-1/-2
拉伸模量 (140°C)
1950
MPa
ISO 527-1/-2
拉伸模量 (160°C)
1870
MPa
ISO 527-1/-2
拉伸模量 (180°C)
1650
MPa
ISO 527-1/-2
拉伸模量 (200°C)
1370
MPa
ISO 527-1/-2
断裂应力
125
MPa
ISO 527-1/-2
断裂伸长率
2.5
%
ISO 527-1/-2
弯曲模量
4700
MPa
ISO 178
弯曲强度
180
MPa
ISO 178
简支梁无缺口冲击强度(+23°C)
50
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(-30°C)
40
kJ/m²
ISO 179/1eU
最大刺穿力(+23°C)
613
N
ISO 6603-2
最大刺穿力（-30°C)
608
N
ISO 6603-2
刺穿能(+23°C)
1.8
J
ISO 6603-2
刺穿能（-30°C)
1.8
J
ISO 6603-2
热性能
熔融温度(10°C/min)
213
°C
ISO 11357-1/-3
热变形温度(1.80 MPa)
190
°C
ISO 75-1/-2
热变形温度(0.45 MPa)
210
°C
ISO 75-1/-2
热变形温度(8.00 MPa)
60
°C
ISO 75-1/-2
线热膨胀系数(平行)
0.3
E-4/°C
ISO 11359-1/-2
线热膨胀系数(垂直)
1.1
E-4/°C
ISO 11359-1/-2
燃烧性（1.5mm厚度）
HB
class
IEC 60695-11-10
测试厚度
1.5
mm
IEC 60695-11-10
厚度为h时的燃烧性
HB
class
IEC 60695-11-10
测试厚度
0.75
mm
IEC 60695-11-10
燃烧性－氧指数
22
%
ISO 4589-1/-2
灼热丝燃烧指数GWFI
650
°C
IEC 60695-2-12
GWFI (厚度(1))
2
mm
IEC 60695-2-12
电性能
相对漏电起痕指数
375
V
IEC 60112
其它性能
吸水率
8.5
%
Sim. to ISO 62
吸湿率
2.6
%
Sim. to ISO 62
密度
1230
kg/m³
ISO 1183
材料特性
粘数
138
cm³/g
ISO 307, 1157, 1628