Durethan® BKV130P 702214
30% 玻纤增强, 注塑成型, 耐冲击改性
通用信息
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
特殊性能
下载
法规
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-06-27
加工工艺
注塑成型
注塑成型
机械性能
拉伸模量
9300
MPa
ISO 527-1/-2
拉伸模量 (-40°C)
9660
MPa
ISO 527-1/-2
拉伸模量 (40°C)
8220
MPa
ISO 527-1/-2
拉伸模量 (100°C)
4150
MPa
ISO 527-1/-2
拉伸模量 (120°C)
3850
MPa
ISO 527-1/-2
拉伸模量 (140°C)
3630
MPa
ISO 527-1/-2
拉伸模量 (160°C)
3470
MPa
ISO 527-1/-2
拉伸模量 (180°C)
3270
MPa
ISO 527-1/-2
拉伸模量 (200°C)
2730
MPa
ISO 527-1/-2
断裂应力
155
MPa
ISO 527-1/-2
断裂应力（120°C)
85
MPa
ISO 527-1/-2
断裂伸长率
4.2
%
ISO 527-1/-2
断裂应变(120°C)
14.5
%
ISO 527-1/-2
弯曲模量
8700
MPa
ISO 178
弯曲强度
260
MPa
ISO 178
简支梁无缺口冲击强度(+23°C)
95
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(-30°C)
85
kJ/m²
ISO 179/1eU
简支梁缺口冲击强度(+23°C)
12
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(-30°C)
10
kJ/m²
ISO 179/1eA
悬臂梁缺口冲击强度(23°C)
14
kJ/m²
ISO 180/1A
热性能
熔融温度(10°C/min)
220
°C
ISO 11357-1/-3
热变形温度(1.80 MPa)
205
°C
ISO 75-1/-2
热变形温度(0.45 MPa)
222
°C
ISO 75-1/-2
其它性能
密度
1360
kg/m³
ISO 1183
材料特性
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
260-280
°C
Mold temperature
80-100
°C