Pocan® BFN4211
13%ガラス強化, 射出成形, 難燃(ハロゲンフリー）
一般情報
Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
特徴
各種規制
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration PFAS (PTFE containing)2024-03-05
- Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- CALIFORNIA PROPOSITION 65 (INDUSTRIAL USE)2024-01-02
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-09-12
- 2024-05-16
Yellow Card
成形方法
Injection Molding
Injection Molding
流動特性
メルトボリュームフローレイト
15
cm³/10min
ISO 1133
温度
260
°C
ISO 1133
荷重
2.16
kg
ISO 1133
成形収縮率 (流れ方向）
0.6
%
ISO 294-4
成形収縮率 (垂直方向)
1.1
%
ISO 294-4
機械特性
引張弾性率
6200
MPa
ISO 527-1/-2
引張弾性率 (-40℃)
7420
MPa
ISO 527-1/-2
引張弾性率 (40°C)
5010
MPa
ISO 527-1/-2
引張弾性率 (100°C)
3140
MPa
ISO 527-1/-2
引張弾性率 (120℃)
2870
MPa
ISO 527-1/-2
引張弾性率 (140℃)
2590
MPa
ISO 527-1/-2
引張弾性率 (160℃)
2300
MPa
ISO 527-1/-2
引張弾性率 (180℃)
1990
MPa
ISO 527-1/-2
引張弾性率 (200℃)
1620
MPa
ISO 527-1/-2
引張破断強度
75
MPa
ISO 527-1/-2
引張破断ひずみ
2.7
%
ISO 527-1/-2
曲げ弾性率
6700
MPa
ISO 178
曲げ強度
125
MPa
ISO 178
Flexural strain at flexural strength
2.7
%
ISO 178-A
シャルピー衝撃強さ (23℃)
30
kJ/m²
ISO 179/1eU
シャルピー衝撃強さ (-30℃)
25
kJ/m²
ISO 179/1eU
アイゾット衝撃強さ ノッチなし (+23℃)
25
kJ/m²
ISO 180/1U
Izod impact strength (-30°C)
23
kJ/m²
ISO 180-1U
熱的特性
融点 (10℃/min)
220
°C
ISO 11357-1/-3
荷重たわみ温度 (1.8MPa)
190
°C
ISO 75-1/-2
荷重たわみ温度 (0.45MPa)
220
°C
ISO 75-1/-2
線膨張係数 (流れ方向)
0.4
E-4/°C
ISO 11359-1/-2
線膨張係数 (垂直方向)
0.9
E-4/°C
ISO 11359-1/-2
厚さhでの燃焼性
V-0
class
IEC 60695-11-10
試験片厚さ
0.75
mm
IEC 60695-11-10
1.5mm厚さでの燃焼性
V-0
class
IEC 60695-11-10
追加試験片の厚さ (1.5)
1.5
mm
IEC 60695-11-10
UL認定
Yes
-
-
厚さhでの燃焼性
V-0
class
IEC 60695-11-10
追加試験片の厚さ(h)
3
mm
IEC 60695-11-10
UL認定
Yes
-
-
厚さhでの燃焼性 5V
5VA
class
IEC 60695-11-20
追加試験片の厚さ(h)
1.5
mm
IEC 60695-11-20
UL認定
Yes
-
-
ボールプレッシャー温度
215
°C
IEC 60695-10-2
グローワイヤ燃焼性指数
960
°C
IEC 60695-2-12
GWFI (厚さ (1))
0.4
mm
IEC 60695-2-12
グローワイヤ燃焼性指数
960
°C
IEC 60695-2-12
GWFI (厚さ (2))
0.75
mm
IEC 60695-2-12
グローワイヤ着火温度
775
°C
IEC 60695-2-13
GWIT (厚さ (1))
0.4
mm
IEC 60695-2-13
グローワイヤ着火温度
775
°C
IEC 60695-2-13
GWIT (厚さ (2))
0.75
mm
IEC 60695-2-13
グローワイヤ着火温度
775
°C
IEC 60695-2-13
GWIT (厚さ (3))
1.5
mm
IEC 60695-2-13
グローワイヤ着火温度
775
°C
IEC 60695-2-13
GWIT (厚さ (4))
3
mm
IEC 60695-2-13
相対温度インデックス-電気
130
°C
UL746B
ＲＴＩ−電気 (厚さ(1))
0.4
mm
UL746B
相対温度インデックス-電気
150
°C
UL746B
ＲＴＩ−電気 (厚さ(2))
0.75
mm
UL746B
相対温度インデックス-衝撃
140
°C
UL746B
ＲＴＩ−衝撃 (厚さ(1))
0.4
mm
UL746B
相対温度インデックス-衝撃なし
150
°C
UL746B
ＲＴＩ−衝撃なし (厚さ(1))
0.4
mm
UL746B
電気特性
体積固有抵抗率
>1E13
Ohm*m
IEC 62631-3-1
絶縁破壊強さ
33.4
kV/mm
IEC 60243-1
耐トラッキング指数
550
V
IEC 60112
耐トラッキング指数 (PLC)
0
class
UL 746A
その他特性
密度
1430
kg/m³
ISO 1183
材料特性
Drying temperature circulating air dryer
120
°C
Drying time circulating air dryer
4-8
h
Residual moisture content
0.00-0.02
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
250-265
°C
Mold temperature
70-90
°C
メルトボリュームフローレイト
15
cm³/10min
ISO 1133
温度
260
°C
ISO 1133
荷重
2.16
kg
ISO 1133
成形収縮率 (流れ方向）
0.6
%
ISO 294-4
成形収縮率 (垂直方向)
1.1
%
ISO 294-4