Pocan® BFN4211 000000

13%ガラス強化, 射出成形, 難燃(ハロゲンフリー）

結果に戻る

一般情報

Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
特徴
ダウンロード
各種規制
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
Yellow Card
成形方法
Injection Molding
お問い合わせ(英語)

流動特性

メルトボリュームフローレイト
15
cm³/10min
温度
260
°C
荷重
2.16
kg
成形収縮率 (流れ方向）
0.6
%
成形収縮率 (垂直方向)
1.1
%

機械特性

引張弾性率
6200
MPa
引張弾性率 (-40℃)
7420
MPa
引張弾性率 (40°C)
5010
MPa
引張弾性率 (100°C)
3140
MPa
引張弾性率 (120℃)
2870
MPa
引張弾性率 (140℃)
2590
MPa
引張弾性率 (160℃)
2300
MPa
引張弾性率 (180℃)
1990
MPa
引張弾性率 (200℃)
1620
MPa
引張破断強度
75
MPa
引張破断ひずみ
2.7
%
曲げ弾性率
6700
MPa
曲げ強度
125
MPa
Flexural strain at flexural strength
2.7
%
シャルピー衝撃強さ (23℃)
30
kJ/m²
シャルピー衝撃強さ (-30℃)
25
kJ/m²
アイゾット衝撃強さ ノッチなし (+23℃)
25
kJ/m²
Izod impact strength (-30°C)
23
kJ/m²

熱的特性

融点 (10℃/min)
220
°C
荷重たわみ温度 (1.8MPa)
190
°C
荷重たわみ温度 (0.45MPa)
220
°C
線膨張係数 (流れ方向)
0.4
E-4/°C
線膨張係数 (垂直方向)
0.9
E-4/°C
1.5mm厚さでの燃焼性
V-0
class
追加試験片の厚さ (1.5)
5VA
mm
厚さhでの燃焼性 5V
5VA
class
追加試験片の厚さ(h)
1.5
mm
ボールプレッシャー温度
215
°C
グローワイヤ燃焼性指数
960
°C
GWFI (厚さ (1))
0.4
mm
グローワイヤ燃焼性指数
960
°C
GWFI (厚さ (2))
0.75
mm
グローワイヤ着火温度
775
°C
GWIT (厚さ (1))
0.4
mm
グローワイヤ着火温度
775
°C
GWIT (厚さ (2))
0.75
mm
グローワイヤ着火温度
775
°C
GWIT (厚さ (3))
1.5
mm
グローワイヤ着火温度
775
°C
GWIT (厚さ (4))
3
mm

電気特性

体積固有抵抗率
>1E13
Ohm*m
絶縁破壊強さ
33.4
kV/mm
耐トラッキング指数
550
V
耐トラッキング指数 (PLC)
0
class

その他特性

密度
1430
kg/m³