Pocan® B7616 000000

15%ガラス強化, 射出成形, 優れた表面特性, 低そり

結果に戻る

一般情報

Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
特徴
  • Good surface properties
  • Low warpage
ダウンロード
各種規制
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
Yellow Card
成形方法
Injection Molding
お問い合わせ(英語)

流動特性

メルトボリュームフローレイト
17
cm³/10min
温度
260
°C
荷重
2.16
kg
成形収縮率 (流れ方向）
0.7
%
成形収縮率 (垂直方向)
0.5
%

機械特性

引張弾性率
4600
MPa
引張弾性率 (-40℃)
4810
MPa
引張弾性率 (40°C)
3830
MPa
引張弾性率 (100°C)
1730
MPa
引張弾性率 (120℃)
1050
MPa
引張弾性率 (140℃)
356
MPa
引張破断強度
75
MPa
引張破断ひずみ
4.2
%
曲げ弾性率
4500
MPa
曲げ強度
130
MPa
Flexural strain at flexural strength
4.7
%
シャルピー衝撃強さ (23℃)
45
kJ/m²
シャルピー衝撃強さ (-30℃)
50
kJ/m²
アイゾット衝撃強さ ノッチなし (+23℃)
35
kJ/m²
Izod impact strength (-30°C)
40
kJ/m²
パンクチャー衝撃−最大応力 (+23℃)
437
N
パンクチャー衝撃エネルギー (+23℃)
1.3
J

熱的特性

融点 (10℃/min)
225
°C
荷重たわみ温度 (1.8MPa)
105
°C
荷重たわみ温度 (0.45MPa)
135
°C
荷重たわみ温度 (8.0MPa)
75
°C
線膨張係数 (流れ方向)
0.5
E-4/°C
線膨張係数 (垂直方向)
0.8
E-4/°C
1.5mm厚さでの燃焼性
HB
class
追加試験片の厚さ (1.5)
1.5
mm
厚さhでの燃焼性
HB
class
試験片厚さ
0.75
mm
ボールプレッシャー温度
150
°C
グローワイヤ燃焼性指数
750
°C
GWFI (厚さ (1))
2
mm

電気特性

比誘電率 (100 Hz)
3.5
-
比誘電率 (1MHz)
3.4
-
誘電正接 (100 Hz)
10
E-4
誘電正接 (1MHz)
130
E-4
体積固有抵抗率
>1E13
Ohm*m
表面抵抗率
>1E15
Ohm
絶縁破壊強さ
34
kV/mm
耐トラッキング指数
200
V

その他特性

吸水率 (水中)
0.4
%
吸湿率 (23℃/50％ RH)
0.1
%
密度
1350
kg/m³

図表