Pocan® B7375 000000

25% White Pigments, 射出成形, 低そり

結果に戻る

一般情報

Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
特徴
  • Low warpage
ダウンロード
各種規制
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
Yellow Card
成形方法
Injection Molding
お問い合わせ(英語)

流動特性

メルトボリュームフローレイト
37
cm³/10min
温度
250
°C
荷重
2.16
kg
成形収縮率 (流れ方向）
1.8
%
成形収縮率 (垂直方向)
1.7
%

機械特性

引張弾性率
3500
MPa
引張弾性率 (-40℃)
4540
MPa
引張弾性率 (40°C)
1930
MPa
引張弾性率 (100°C)
604
MPa
引張弾性率 (120℃)
511
MPa
引張弾性率 (140℃)
425
MPa
引張弾性率 (160℃)
344
MPa
引張弾性率 (180℃)
275
MPa
引張弾性率 (200℃)
212
MPa
引張破断強度
55
MPa
引張破断ひずみ
3
%
引張クリープ弾性率 (1h)
3400
MPa
引張クリープ弾性率 (1000h)
2700
MPa
曲げ弾性率
3400
MPa
曲げ強度
95
MPa
Flexural strain at flexural strength
5
%
シャルピー衝撃強さ (23℃)
65
kJ/m²
シャルピー衝撃強さ (-30℃)
50
kJ/m²
アイゾット衝撃強さ ノッチなし (+23℃)
60
kJ/m²
Izod impact strength (-30°C)
45
kJ/m²
パンクチャー衝撃エネルギー (+23℃)
3.2
J

熱的特性

融点 (10℃/min)
225
°C
荷重たわみ温度 (1.8MPa)
75
°C
荷重たわみ温度 (0.45MPa)
165
°C
荷重たわみ温度 (8.0MPa)
50
°C
線膨張係数 (流れ方向)
1
E-4/°C
線膨張係数 (垂直方向)
1
E-4/°C
1.5mm厚さでの燃焼性
HB
class
追加試験片の厚さ (1.5)
1.5
mm
厚さhでの燃焼性
HB
class
試験片厚さ
0.75
mm
酸素指数
20
%
ボールプレッシャー温度
200
°C
グローワイヤ燃焼性指数
650
°C
GWFI (厚さ (1))
2
mm

電気特性

比誘電率 (100 Hz)
4.5
-
比誘電率 (1MHz)
4.2
-
誘電正接 (100 Hz)
30
E-4
誘電正接 (1MHz)
170
E-4
体積固有抵抗率
>1E13
Ohm*m
絶縁破壊強さ
26
kV/mm
耐トラッキング指数
450
V

その他特性

吸水率 (水中)
0.4
%
吸湿率 (23℃/50％ RH)
0.2
%
密度
1570
kg/m³

材料特性

粘度数
105
cm³/g

図表