Pocan® B1700 000000

非強化, 押出, フードコンタクト

結果に戻る

一般情報

Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
特徴
ダウンロード
各種規制
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
成形方法
Extrusion
お問い合わせ(英語)

流動特性

メルトボリュームフローレイト
8
cm³/10min
温度
250
°C
荷重
2.16
kg

機械特性

引張弾性率
2600
MPa
引張弾性率 (-40℃)
2920
MPa
引張弾性率 (40°C)
1580
MPa
引張弾性率 (100°C)
356
MPa
引張弾性率 (120℃)
298
MPa
引張弾性率 (140℃)
251
MPa
引張弾性率 (160℃)
217
MPa
引張弾性率 (180℃)
190
MPa
引張弾性率 (200℃)
163
MPa
引張降伏強度
55
MPa
引張降伏ひずみ
4
%
引張破断呼びひずみ
>50
%
曲げ強度
85
MPa
Flexural strain at flexural strength
6
%
シャルピー衝撃強さ (23℃)
N
kJ/m²
シャルピー衝撃強さ (-30℃)
230
kJ/m²
アイゾット衝撃強さ ノッチなし (+23℃)
N
kJ/m²
Izod impact strength (-30°C)
180
kJ/m²
パンクチャー衝撃−最大応力 (+23℃)
3880
N
パンクチャー衝撃−最大応力 (-30℃)
3930
N
パンクチャー衝撃エネルギー (+23℃)
23
J
パンクチャー衝撃エネルギー (-30℃)
16
J

熱的特性

融点 (10℃/min)
225
°C
荷重たわみ温度 (1.8MPa)
60
°C
荷重たわみ温度 (0.45MPa)
140
°C
荷重たわみ温度 (8.0MPa)
45
°C
線膨張係数 (流れ方向)
1.3
E-4/°C
線膨張係数 (垂直方向)
1.3
E-4/°C
1.5mm厚さでの燃焼性
HB
class
追加試験片の厚さ (1.5)
1.5
mm
厚さhでの燃焼性
HB
class
試験片厚さ
0.75
mm

電気特性

比誘電率 (100 Hz)
3.4
-
比誘電率 (1MHz)
3.2
-
誘電正接 (100 Hz)
15
E-4
誘電正接 (1MHz)
200
E-4
体積固有抵抗率
>1E13
Ohm*m
表面抵抗率
>1E15
Ohm
絶縁破壊強さ
30
kV/mm
耐トラッキング指数
600
V

その他特性

吸水率 (水中)
0.5
%
吸湿率 (23℃/50％ RH)
0.2
%
密度
1300
kg/m³

材料特性

粘度数
158
cm³/g