Pocan® B1100 000000

非強化, 射出成形, 押出, フードコンタクト, 流動性改良

結果に戻る

一般情報

Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
特徴
  • Good or high flow
ダウンロード
各種規制
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
成形方法
Extrusion, Injection Molding
お問い合わせ(英語)

流動特性

メルトボリュームフローレイト
80
cm³/10min
温度
250
°C
荷重
2.16
kg

機械特性

引張弾性率
2700
MPa
曲げ弾性率
2750
MPa
曲げ強度
85
MPa
Flexural strain at flexural strength
6
%
シャルピー衝撃強さ (23℃)
130
kJ/m²
シャルピー衝撃強さ (-30℃)
90
kJ/m²
アイゾット衝撃強さ ノッチなし (+23℃)
90
kJ/m²
Izod impact strength (-30°C)
75
kJ/m²

熱的特性

融点 (10℃/min)
225
°C
荷重たわみ温度 (1.8MPa)
60
°C
荷重たわみ温度 (0.45MPa)
160
°C
線膨張係数 (流れ方向)
1.3
E-4/°C
線膨張係数 (垂直方向)
1.3
E-4/°C
1.5mm厚さでの燃焼性
HB
class
追加試験片の厚さ (1.5)
1.5
mm
厚さhでの燃焼性
HB
class
試験片厚さ
0.75
mm
酸素指数
24
%
ボールプレッシャー温度
190
°C

電気特性

比誘電率 (100 Hz)
3.4
-
比誘電率 (1MHz)
3.2
-
誘電正接 (100 Hz)
20
E-4
誘電正接 (1MHz)
190
E-4
体積固有抵抗率
>1E13
Ohm*m
表面抵抗率
>1E15
Ohm

その他特性

吸水率 (水中)
0.5
%
吸湿率 (23℃/50％ RH)
0.2
%
密度
1300
kg/m³