Pocan® AF4110 000000

12%ガラス強化, 射出成形, 難燃, 低そり

結果に戻る

一般情報

Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
特徴
  • Low warpage
ダウンロード
各種規制
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
Yellow Card
成形方法
Injection Molding
お問い合わせ(英語)

流動特性

メルトボリュームフローレイト
35
cm³/10min
温度
260
°C
荷重
5
kg
成形収縮率 (流れ方向）
0.9
%
成形収縮率 (垂直方向)
0.8
%

機械特性

引張弾性率
5800
MPa
引張弾性率 (-40℃)
5820
MPa
引張弾性率 (40°C)
4350
MPa
引張弾性率 (100°C)
2520
MPa
引張弾性率 (120℃)
1390
MPa
引張弾性率 (140℃)
1040
MPa
引張弾性率 (160℃)
669
MPa
引張弾性率 (180℃)
420
MPa
引張破断強度
85
MPa
引張破断ひずみ
2.5
%
曲げ弾性率
5500
MPa
曲げ強度
135
MPa
Flexural strain at flexural strength
2.8
%
シャルピー衝撃強さ (23℃)
35
kJ/m²
アイゾット衝撃強さ ノッチなし (+23℃)
30
kJ/m²

熱的特性

融点 (10℃/min)
225
°C
荷重たわみ温度 (1.8MPa)
130
°C
荷重たわみ温度 (0.45MPa)
204
°C
1.5mm厚さでの燃焼性
V-0
class
追加試験片の厚さ (1.5)
1.5
mm
厚さhでの燃焼性
V-0
class
試験片厚さ
0.75
mm
グローワイヤ燃焼性指数
960
°C
GWFI (厚さ (1))
0.75
mm
グローワイヤ燃焼性指数
960
°C
GWFI (厚さ (2))
1.5
mm
グローワイヤ着火温度
725
°C
GWIT (厚さ (1))
0.75
mm
グローワイヤ着火温度
700
°C
GWIT (厚さ (2))
1.5
mm
グローワイヤ着火温度
700
°C
GWIT (厚さ (3))
3
mm

電気特性

耐トラッキング指数
250
V

その他特性

密度
1480
kg/m³

図表