Durethan® BKV115H3.0 000000

15%ガラス強化, 射出成形, 熱安定, 耐衝撃性改良

結果に戻る

一般情報

Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
特徴
  • Heat stabilized
ダウンロード
各種規制
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Conflict minerals declaration (EICC, GeSI)2024-03-21
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
Yellow Card
成形方法
Injection Molding
お問い合わせ(英語)

流動特性

成形収縮率 (流れ方向）
0.4
%
成形収縮率 (垂直方向)
0.5
%

機械特性

引張弾性率
5600
MPa
引張弾性率 (-40℃)
5910
MPa
引張弾性率 (40°C)
4550
MPa
引張弾性率 (100°C)
1990
MPa
引張弾性率 (120℃)
1860
MPa
引張弾性率 (140℃)
1810
MPa
引張弾性率 (160℃)
1740
MPa
引張弾性率 (180℃)
1610
MPa
引張弾性率 (200℃)
1300
MPa
引張破断強度
110
MPa
引張破断ひずみ
4.5
%
曲げ弾性率
5200
MPa
曲げ強度
180
MPa
シャルピー衝撃強さ (23℃)
60
kJ/m²
シャルピー衝撃強さ (-30℃)
45
kJ/m²
シャルピー衝撃強さ ノッチ付き (23℃)
kJ/m²
アイゾット衝撃強さ ノッチ付き (23℃)
kJ/m²
パンクチャー衝撃−最大応力 (+23℃)
700
N
パンクチャー衝撃−最大応力 (-30℃)
600
N
パンクチャー衝撃エネルギー (+23℃)
2
J
パンクチャー衝撃エネルギー (-30℃)
1.6
J

熱的特性

融点 (10℃/min)
212
°C
荷重たわみ温度 (1.8MPa)
185
°C
荷重たわみ温度 (0.45MPa)
205
°C
線膨張係数 (流れ方向)
0.3
E-4/°C
線膨張係数 (垂直方向)
1.2
E-4/°C
1.5mm厚さでの燃焼性
HB
class
追加試験片の厚さ (1.5)
1.5
mm
厚さhでの燃焼性
HB
class
試験片厚さ
0.75
mm
グローワイヤ燃焼性指数
650
°C
GWFI (厚さ (1))
2
mm

電気特性

耐トラッキング指数
600
V

その他特性

吸水率 (水中)
8.5
%
吸湿率 (23℃/50％ RH)
2.5
%
密度
1230
kg/m³

材料特性

粘度数
134
cm³/g

図表