Durethan® BKV15H3.0 DUS008
15%ガラス強化, 射出成形, 熱安定
一般情報
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
特徴
- Heat stabilized
各種規制
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration PFAS2024-03-05
- Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Compliance Statement EU Sanctions and Embargos2024-05-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
成形方法
Injection Molding
Injection Molding
機械特性
引張弾性率
6500
MPa
ISO 527-1/-2
引張弾性率 (-40℃)
6460
MPa
ISO 527-1/-2
引張弾性率 (40°C)
5510
MPa
ISO 527-1/-2
引張弾性率 (100°C)
2470
MPa
ISO 527-1/-2
引張弾性率 (120℃)
2330
MPa
ISO 527-1/-2
引張弾性率 (140℃)
2220
MPa
ISO 527-1/-2
引張弾性率 (160℃)
2100
MPa
ISO 527-1/-2
引張弾性率 (180℃)
1960
MPa
ISO 527-1/-2
引張弾性率 (200℃)
1810
MPa
ISO 527-1/-2
引張破断強度
130
MPa
ISO 527-1/-2
引張破断ひずみ
3
%
ISO 527-1/-2
曲げ弾性率
5500
MPa
ISO 178
曲げ強度
205
MPa
ISO 178
シャルピー衝撃強さ (23℃)
50
kJ/m²
ISO 179/1eU
シャルピー衝撃強さ (-30℃)
45
kJ/m²
ISO 179/1eU
アイゾット衝撃強さ ノッチ付き (23℃)
kJ/m²
ISO 180/1A
熱的特性
融点 (10℃/min)
220
°C
ISO 11357-1/-3
荷重たわみ温度 (1.8MPa)
195
°C
ISO 75-1/-2
荷重たわみ温度 (0.45MPa)
215
°C
ISO 75-1/-2
線膨張係数 (流れ方向)
0.3
E-4/°C
ISO 11359-1/-2
線膨張係数 (垂直方向)
1
E-4/°C
ISO 11359-1/-2
厚さhでの燃焼性
HB
class
IEC 60695-11-10
厚さhでの燃焼性
HB
class
IEC 60695-11-10
その他特性
密度
1230
kg/m³
ISO 1183
材料特性
乾燥温度
80
°C
ドライエアーでの乾燥時間
2-6
h
残留水分量
0.03-0.12
%
acc. to Karl Fischer
溶融温度 (Tmin - Tmax)
260-290
°C
金型温度
80-100
°C