Durethan® BCF30H2.0EF
30% Carbon Reinforced, 射出成形, 熱安定, 流動性改良
一般情報
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
特徴
- Good or high flow
- Heat stabilized
各種規制
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration PFAS2024-03-05
- Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Compliance Statement EU Sanctions and Embargos2024-05-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-11-08
成形方法
Injection Molding
Injection Molding
流動特性
成形収縮率 (流れ方向）
0.1
%
ISO 294-4
成形収縮率 (垂直方向)
0.45
%
ISO 294-4
機械特性
引張弾性率
23000
MPa
ISO 527-1/-2
引張弾性率 (-40℃)
24300
MPa
ISO 527-1/-2
引張弾性率 (40°C)
18200
MPa
ISO 527-1/-2
引張弾性率 (100°C)
8650
MPa
ISO 527-1/-2
引張弾性率 (120℃)
8000
MPa
ISO 527-1/-2
引張弾性率 (140℃)
7490
MPa
ISO 527-1/-2
引張弾性率 (160℃)
6990
MPa
ISO 527-1/-2
引張弾性率 (180℃)
6030
MPa
ISO 527-1/-2
引張弾性率 (200℃)
4950
MPa
ISO 527-1/-2
引張破断強度
225
MPa
ISO 527-1/-2
引張破断ひずみ
1.7
%
ISO 527-1/-2
曲げ弾性率
20500
MPa
ISO 178
曲げ強度
330
MPa
ISO 178
シャルピー衝撃強さ (23℃)
50
kJ/m²
ISO 179/1eU
シャルピー衝撃強さ (-30℃)
45
kJ/m²
ISO 179/1eU
シャルピー衝撃強さ ノッチ付き (23℃)
kJ/m²
ISO 179/1eA
アイゾット衝撃強さ ノッチ付き (23℃)
kJ/m²
ISO 180/1A
パンクチャー衝撃−最大応力 (+23℃)
850
N
ISO 6603-2
パンクチャー衝撃−最大応力 (-30℃)
675
N
ISO 6603-2
パンクチャー衝撃エネルギー (+23℃)
1.7
J
ISO 6603-2
パンクチャー衝撃エネルギー (-30℃)
1
J
ISO 6603-2
熱的特性
融点 (10℃/min)
221
°C
ISO 11357-1/-3
荷重たわみ温度 (1.8MPa)
210
°C
ISO 75-1/-2
荷重たわみ温度 (0.45MPa)
220
°C
ISO 75-1/-2
線膨張係数 (流れ方向)
0.1
E-4/°C
ISO 11359-1/-2
線膨張係数 (垂直方向)
0.9
E-4/°C
ISO 11359-1/-2
その他特性
吸水率 (水中)
7.5
%
Sim. to ISO 62
吸湿率 (23℃/50％ RH)
2.2
%
Sim. to ISO 62
密度
1260
kg/m³
ISO 1183
材料特性
乾燥温度
80
°C
ドライエアーでの乾燥時間
2-6
h
残留水分量
0.02-0.12
%
acc. to Karl Fischer
溶融温度 (Tmin - Tmax)
270-290
°C
金型温度
80-120
°C