Xytron™ TC6022I

Thermal conductive material

Back to results

General Information

Xytron™ is a high performance plastic compound of Envalior, which is based on PPS (polyphenylene sulphide).
Xytron™ offers extremely good chemical resistance, dimensional stability, intrinsic flame retardancy and high stiffness.
Because of its outstanding properties, Xytron™ contributes to an excellent performance in many different applications.
Special features
  • Thermal conductive
General Document
Regulatory Affairs
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Compliance Statement EU Sanctions and Embargos2024-05-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Design challenge
Degradation & Stability | Chemical stability
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
0.2
%
Molding shrinkage (normal)
0.5
%

Mechanical properties

Tensile modulus
22000
MPa
Tensile modulus (-40°C)
23000
MPa
Tensile modulus (120°C)
12200
MPa
Tensile modulus (160°C)
9900
MPa
Tensile modulus (180°C)
9150
MPa
Stress at break
120
MPa
Stress at break (-40°C)
138
MPa
Stress at break (120°C)
78.5
MPa
Stress at break (160°C)
63
MPa
Stress at break (180°C)
55
MPa
Strain at break
0.7
%
Strain at break (-40°C)
0.75
%
Strain at break (120°C)
1.2
%
Strain at break (160°C)
1.5
%
Strain at break (180°C)
1.3
%
Flexural modulus
23200
MPa
Flexural modulus (120°C)
13800
MPa
Flexural modulus (160°C)
11000
MPa
Flexural modulus (180°C)
10100
MPa
Flexural strength
215
MPa
Flexural strength (120°C)
140
MPa
Flexural strength (160°C)
110
MPa
Flexural strength (180°C)
95
MPa
Charpy impact strength (+23°C)
16
kJ/m²
Charpy impact strength (-30°C)
16
kJ/m²
Charpy notched impact strength (+23°C)
9
kJ/m²
Charpy notched impact strength (-30°C)
9
kJ/m²
Weldline strength at thickness 1
23
MPa
Weldline strain at thickness 1
0.1
%
Thickness tested (1)
4
mm
Rockwell hardness, R scale
120
-
Rockwell hardness, M scale
100
-

Thermal properties

Melting temperature (10°C/min)
280
°C
Glass transition temperature (10°C/min)
90
°C
Temp. of deflection under load (1.80 MPa)
265
°C
Coeff. of linear therm. expansion (parallel)
0.11
E-4/°C
Coeff. of linear therm. expansion (normal)
0.3
E-4/°C
Coef. of lin. therm expansion, parallel, above Tg
0.12
E-4/°C
Coef. of lin. therm expansion, normal, above Tg
0.72
E-4/°C
Thermal conductivity in plane
2.2
W/(m K)
Thermal conductivity through plane
1.2
W/(m K)
Burning Behav. at 3.0 mm nom. thickn.
V-0
class
Thickness tested
3
mm
UL recognition
Yes
-
Relative Temperature Index - electrical
130
°C
RTI electrical (Thickness (1) tested)
0.4
mm
Relative Temperature Index - electrical
130
°C
RTI electrical (Thickness (2) tested)
3
mm
Relative Temperature Index - with impact
130
°C
RTI with impact (Thickness (1) tested)
0.4
mm
Relative Temperature Index - with impact
130
°C
RTI with impact (Thickness (2) tested)
3
mm
Relative Temperature Index - without impact
130
°C
RTI without impact (Thickness (1) tested)
0.4
mm
Relative Temperature Index - without impact
130
°C
RTI without impact (Thickness (2) tested)
3
mm

Electrical properties

Volume resistivity
>1E13
Ohm*m
Surface resistivity
>1E15
Ohm
Comparative tracking index
225
V

Other properties

Water absorption in water at 23°C after 24h
0.04
%
Density
1850
kg/m³

Diagrams