Xytron™ G3080E

30% Glass Reinforced, Improved Impact

Back to results

General Information

Xytron™ is a high performance plastic compound of Envalior, which is based on PPS (polyphenylene sulphide).
Xytron™ offers extremely good chemical resistance, dimensional stability, intrinsic flame retardancy and high stiffness.
Because of its outstanding properties, Xytron™ contributes to an excellent performance in many different applications.
Special features
General Document
Processing technology
Injection Molding
Design challenge
Degradation & Stability | Chemical stability
Automotive OEM
PSA
OEM Specification
STELLANTIS - 01994-16-00164-MAN-01378-20-00213-(2021-07)
Applications
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
0.2
%
Molding shrinkage (normal)
0.65
%
Spiral flow length 1.0 mm 1000 bar
98
mm

Mechanical properties

Tensile modulus
9300
MPa
Tensile modulus (-40°C)
9800
MPa
Tensile modulus (120°C)
4500
MPa
Tensile modulus (160°C)
2500
MPa
Tensile modulus (200°C)
1900
MPa
Stress at break
140
MPa
Stress at break (-40°C)
165
MPa
Stress at break (120°C)
63
MPa
Stress at break (160°C)
48
MPa
Stress at break (200°C)
45
MPa
Strain at break
2.5
%
Strain at break (-40°C)
2.5
%
Strain at break (120°C)
6.8
%
Strain at break (160°C)
8.5
%
Strain at break (200°C)
9
%
Flexural modulus
7900
MPa
Flexural modulus (120°C)
6800
MPa
Flexural modulus (160°C)
2800
MPa
Flexural modulus (200°C)
2300
MPa
Flexural strength
205
MPa
Flexural strength (120°C)
88
MPa
Flexural strength (160°C)
55
MPa
Flexural strength (200°C)
46
MPa
Charpy impact strength (+23°C)
55
kJ/m²
Charpy impact strength (-30°C)
60
kJ/m²
Charpy notched impact strength (+23°C)
16
kJ/m²
Charpy notched impact strength (-30°C)
11
kJ/m²
Izod impact strength (+23°C)
55
kJ/m²
Izod notched impact strength (+23°C)
16.5
kJ/m²
Weldline strength at thickness 1
58
MPa
Weldline strain at thickness 1
0.9
%
Thickness tested (1)
4
mm

Thermal properties

Melting temperature (10°C/min)
280
°C
Glass transition temperature (10°C/min)
90
°C
Temp. of deflection under load (1.80 MPa)
250
°C
Coeff. of linear therm. expansion (parallel)
0.15
E-4/°C
Coeff. of linear therm. expansion (normal)
0.57
E-4/°C
Coef. of lin. therm expansion, parallel, above Tg
0.15
E-4/°C
Coef. of lin. therm expansion, normal, above Tg
1.26
E-4/°C

Electrical properties

Volume resistivity
>1E13
Ohm*m
Surface resistivity
>1E15
Ohm

Other properties

Density
1460
kg/m³

Diagrams

Applications

Accumulator Piston

Industry
Automotive
Material
  • •} Part consolidation of bushings/housing
  • •} From 3 parts to a 1 piece design
  • •} Lightweight
  • •} Wear resistant
  • •} High temperature performance
  • •} Fatigue resistance
  • •} Chemical resistance
  • •} Improved energy efficiency
}
More information

ADAS Radar Housing

Industry
Automotive
Material
Envalior offers many solutions for today’s complex ADAS components, including proven material solutions such as Arnite® PBT. New Xytron™ PPS material solutions are also being developed to deliver more affordable performance compared to polyetherimide (PEI) thermoplastics.}
More information

Electrical water pump

Industry
Automotive
Material
  • •} Coolant resistivity, dimensional stable
  • •} Low mositure up-take and permeation
  • •} Thermal shock resistivity​
  • •} High and stable dielectric strength
  • •} Enhances zero emission mobility of BEV
}