Xytron™ G4010E

40% Glass Reinforced, Improved Impact

Back to results

General Information

Xytron™ is a high performance plastic compound of Envalior, which is based on PPS (polyphenylene sulphide).
Xytron™ offers extremely good chemical resistance, dimensional stability, intrinsic flame retardancy and high stiffness.
Because of its outstanding properties, Xytron™ contributes to an excellent performance in many different applications.
Special features
General Document
Regulatory Affairs
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Compliance Statement EU Sanctions and Embargos2024-05-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Design challenge
Degradation & Stability | Chemical stability
Applications
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
0.2
%
Molding shrinkage (normal)
0.5
%
Spiral flow length 1.0 mm 1000 bar
105
mm

Mechanical properties

Tensile modulus
12000
MPa
Tensile modulus (-40°C)
13500
MPa
Tensile modulus (120°C)
6100
MPa
Tensile modulus (160°C)
3900
MPa
Tensile modulus (200°C)
3000
MPa
Stress at break
160
MPa
Stress at break (-40°C)
205
MPa
Stress at break (120°C)
65
MPa
Stress at break (160°C)
50
MPa
Stress at break (200°C)
40
MPa
Strain at break
2.4
%
Strain at break (-40°C)
2.4
%
Strain at break (120°C)
3.9
%
Strain at break (160°C)
4.4
%
Strain at break (200°C)
4.5
%
Flexural modulus
10000
MPa
Flexural modulus (120°C)
8500
MPa
Flexural modulus (160°C)
4600
MPa
Flexural modulus (200°C)
3100
MPa
Flexural strength
230
MPa
Flexural strength (120°C)
120
MPa
Flexural strength (160°C)
70
MPa
Flexural strength (200°C)
50
MPa
Charpy impact strength (+23°C)
55
kJ/m²
Charpy impact strength (-30°C)
65
kJ/m²
Charpy notched impact strength (+23°C)
16
kJ/m²
Charpy notched impact strength (-30°C)
12
kJ/m²
Izod impact strength (+23°C)
60
kJ/m²
Izod notched impact strength (+23°C)
17.5
kJ/m²
Izod notched impact strength (-40°C)
13
kJ/m²
Weldline strength at thickness 1
55
MPa
Weldline strain at thickness 1
0.7
%
Thickness tested (1)
4
mm

Thermal properties

Melting temperature (10°C/min)
280
°C
Glass transition temperature (10°C/min)
90
°C
Temp. of deflection under load (1.80 MPa)
258
°C
Temp. of deflection under load (0.45 MPa)
279
°C
Temp. of deflection under load (8.00 MPa)
153
°C
Coeff. of linear therm. expansion (parallel)
0.15
E-4/°C
Coeff. of linear therm. expansion (normal)
0.55
E-4/°C
Coef. of lin. therm expansion, parallel, above Tg
0.11
E-4/°C
Coef. of lin. therm expansion, normal, above Tg
1.1
E-4/°C
Glow Wire Flammability Index GWFI
850
°C
GWFI (Thickness (1) tested)
0.8
mm
Glow Wire Ignition Temperature GWIT
825
°C
GWIT (Thickness (1) tested)
0.8
mm

Electrical properties

Relative permittivity (1GHz)
3.8
-
Relative permittivity (5GHz)
3.8
-
Dissipation factor (1GHz)
35
E-4
Dissipation factor (5GHz)
55
E-4
Volume resistivity
>1E13
Ohm*m
Surface resistivity
>1E15
Ohm
Electric strength
33
kV/mm
Comparative tracking index
175
V

Other properties

Water absorption in water at 23°C after 24h
0.04
%
Humidity absorption
0.04
%
Density
1530
kg/m³

Diagrams

Applications

Automotive e-motor Bobbins

Industry
Automotive
Material
  • •} Stanyl® PA46 also used in connectors, e-motor parts, bobbins, sensors, fuse boxes. Thermoconductive Stanyl XL-T (P968A) in use as well
  • •} ForTii® PA4T and Xytron™ PPS also materials to be used in electromotor applications
}
More information