Tensile modulus, low thickness
9000
MPa
ISO 527-1/-2
Tens. Mod. (Thickness tested)
1
mm
ISO 527-1/-2
Stress at break, at low thickness
70
MPa
ISO 527-1/-2
Stress at break (Thickness tested)
1
mm
ISO 527-1/-2
Strain at break, at low thickness
1.2
%
ISO 527-1/-2
Strain at break (Thickness tested)
1
mm
ISO 527-1/-2
Flexural strength (120°C)
60
MPa
ISO 178
Flexural strength (160°C)
45
MPa
ISO 178
Charpy impact strength (+23°C)
10
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
10
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
4
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
4
kJ/m²
ISO 179/1eA
Weldline strength at thickness 1
13
MPa
ISO 527-1/-2
Weldline strain at thickness 1
17
%
ISO 527-1/-2
Weldline strength at thickness 2
0.21
MPa
ISO 527-1/-2
Weldline strain at thickness 2
0.28
%
ISO 527-1/-2