Stanyl® TS272A1

Aramid fibre reinforced, Wear and Friction Modified

Back to results

General Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Product
Stanyl® TS272A1 is a aramid-reinforced friction-modified high heat polyamide that offers extremely low abrasion for gear & bushing applications
Special features
  • Wear and friction modified
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS (PTFE containing)2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
  • Compliance Statement EU Sanctions and Embargos2024-05-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Processing technology
Injection Molding
Design challenge
Wear & Friction
Automotive OEM
CALLOUT, GM
OEM Specification
ASTM D6779 PA0650 B24280
GMW15702-024471-PA46-AF
Applications
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
2.2
%
Molding shrinkage (normal)
2.2
%

Mechanical properties

Tensile modulus
2800
MPa
Tensile modulus (-40°C)
3400
MPa
Tensile modulus (120°C)
780
MPa
Tensile modulus (160°C)
630
MPa
Tensile modulus (180°C)
590
MPa
Tensile modulus (200°C)
560
MPa
Yield stress
MPa
Yield stress (120°C)
44
MPa
Yield stress (160°C)
36
MPa
Yield stress (180°C)
33
MPa
Yield stress (200°C)
30
MPa
Yield strain
%
Nominal strain at break
%
Nominal strain at break (120°C)
>50
%
Nominal strain at break (160°C)
>50
%
Nominal strain at break (180°C)
>50
%
Nominal strain at break (200°C)
>50
%
Stress at break
80
MPa
Stress at break (-40°C)
105
MPa
Strain at break
16
%
Strain at break (-40°C)
7
%
Flexural modulus
2800
MPa
Flexural modulus (120°C)
800
MPa
Flexural modulus (160°C)
700
MPa
Flexural strength
100
MPa
Flexural strength (120°C)
25
MPa
Flexural strength (160°C)
20
MPa
Charpy impact strength (+23°C)
87
kJ/m²
Charpy impact strength (-30°C)
60
kJ/m²
Charpy notched impact strength (+23°C)
5
kJ/m²
Charpy notched impact strength (-30°C)
3
kJ/m²
Weldline strength at thickness 1
71
MPa
Weldline strain at thickness 1
4
%
Thickness tested (1)
4
mm

Thermal properties

Melting temperature (10°C/min)
295
°C
Glass transition temperature (10°C/min)
75
°C
Temp. of deflection under load (1.80 MPa)
160
°C

Other properties

Water absorption
11.3
%
Water absorption in water at 23°C after 24h
3.1
%
Humidity absorption
3
%
Density
1260
kg/m³

JSON SPT

Molding shrinkage (parallel)
2.2
%
Molding shrinkage (normal)
2.2
%

Diagrams

Applications

Front End Accessory Drive Parts: Belt Tensioner,Damping bands, Shoes and Bushings

Industry
Automotive
Material
  • •} Allows for lightweight and more economical solutions
  • •} Allows for more reliable solutions
  • •} Provides higher stiffness and chemical resistance
}
More information