Stanyl® HFX82S

45% Glass Reinforced, Halogen free and free of red phosphorous

Back to results

General Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Product
Stanyl® HFX82S is an electro-friendly & halogen-free flame-retarded high heat polyamide that offers an excellent combination of high CTI, flow and weld-line strength. HFX-grades are often used in connectors such as USB type C.
Special features
  • Phosphorous free
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
  • Compliance Statement EU Sanctions and Embargos2024-05-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Design challenge
Downsizing & Miniaturization
Flame Retardancy | Halogen free
Applications
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
0.3
%
Molding shrinkage (normal)
0.9
%
Spiral flow length 1.0 mm 800 bar
125
mm
Spiral flow length 1.0 mm 900 bar
137
mm
Spiral flow length 1.0 mm 1000 bar
150
mm

Mechanical properties

Tensile modulus
15200
MPa
Tensile modulus (120°C)
7700
MPa
Tensile modulus (160°C)
6500
MPa
Tensile modulus, low thickness
15000
MPa
Tens. Mod. (Thickness tested)
1
mm
Stress at break
180
MPa
Stress at break (120°C)
100
MPa
Stress at break (160°C)
80
MPa
Stress at break, at low thickness
170
MPa
Stress at break (Thickness tested)
1
mm
Strain at break
2.2
%
Strain at break (120°C)
3.5
%
Strain at break (160°C)
3.5
%
Strain at break, at low thickness
2.2
%
Strain at break (Thickness tested)
1
mm
Flexural modulus
14000
MPa
Flexural modulus (120°C)
8300
MPa
Flexural modulus (160°C)
7300
MPa
Flexural strength
255
MPa
Flexural strength (120°C)
150
MPa
Flexural strength (160°C)
120
MPa
Charpy impact strength (+23°C)
70
kJ/m²
Charpy notched impact strength (+23°C)
13
kJ/m²
Weldline strength at thickness 1
42
MPa
Weldline strain at thickness 1
0.4
%
Thickness tested (1)
4
mm
Weldline strength at thickness 2
50
MPa
Weldline strain at thickness 2
0.47
%
Thickness tested (2)
1
mm

Thermal properties

Melting temperature (10°C/min)
286
°C
Temp. of deflection under load (1.80 MPa)
276
°C
Temp. of deflection under load (0.45 MPa)
282
°C
Burning Behav. at 3.0 mm nom. thickn.
V-0
class
Thickness tested
3
mm
UL recognition
Yes
-
Glow Wire Flammability Index GWFI
960
°C
GWFI (Thickness (1) tested)
3
mm
Glow Wire Flammability Index GWFI
960
°C
GWFI (Thickness (2) tested)
0.8
mm
Glow Wire Ignition Temperature GWIT
825
°C
GWIT (Thickness (1) tested)
3
mm
Glow Wire Ignition Temperature GWIT
800
°C
GWIT (Thickness (2) tested)
1.6
mm

Electrical properties

Relative permittivity (1GHz)
4.2
-
Dissipation factor (1GHz)
100
E-4
Electric strength
40
kV/mm
Comparative tracking index
600
V

Other properties

Water absorption in water at 23°C after 24h
1.6
%
Humidity absorption
1.6
%
Density
1600
kg/m³

Diagrams

Applications

DDR DIMM Connectors

Industry
Electronics
Material
  • •} Sustainable solution due to good carbon footprint
  • •} Flame retardant
  • •} Halogen-free
  • •} Red-phosphorous free
}
More information

Robotic connectors & circuitry

Industry
Robotics
Material
  • •} Stanyl® and ForTii® are proven solutions for connectors used by many of the world's leading automakers and electronics manufacturers.
  • •} Superior strength and durability vs liquid crystal polymers (LCP) and other thermoplastics.
  • •} Material solutions formulated for laser direct structuring for precision processing.
}
More information

USB-C Connectors

Industry
Electronics
Material
  • •} Glass-reinforced
  • •} Provides up to 50% more wear resistance compared to other high temperature polyamides
  • •} Enables thinner wall designs
  • •} Halogen and red phosphorous-free grades are available
}
More information