Stanyl® Diablo OCD2100

40% Glass Reinforced, Heat Stabilized

Back to results

General Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Special features
  • Heat stabilized
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
  • Compliance Statement EU Sanctions and Embargos2024-05-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Processing technology
Injection Molding
Design challenge
Degradation & Stability | Thermo-oxidative stability
Automotive OEM
CALLOUT, FIAT CHRYSLER, GM, PSA, RENAULT
OEM Specification
ASTM D6779 PA0620G40A54400
FCA-MS50017(MS-DB-41)-CPN5044-(2017-02)
FEM 03-20-007--B
GMW15702-013591-PA46-GF40
SPA X62 4554
STELLANTIS - 01994-16-00164-MAN-01994-10-00343-(2021-07)
Applications
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
0.5
%
Molding shrinkage (normal)
1
%
Spiral flow length 1.0 mm 800 bar
90
mm
Spiral flow length 1.0 mm 900 bar
100
mm
Spiral flow length 1.0 mm 1000 bar
110
mm

Mechanical properties

Tensile modulus
13000
MPa
Tensile modulus (120°C)
5000
MPa
Tensile modulus (160°C)
4600
MPa
Tensile modulus (180°C)
4200
MPa
Tensile modulus (200°C)
3400
MPa
Stress at break
210
MPa
Stress at break (120°C)
100
MPa
Stress at break (160°C)
85
MPa
Stress at break (180°C)
75
MPa
Stress at break (200°C)
60
MPa
Strain at break
3
%
Strain at break (120°C)
10
%
Strain at break (160°C)
11
%
Strain at break (180°C)
12
%
Strain at break (200°C)
12.5
%
Flexural modulus
13000
MPa
Flexural modulus (120°C)
5000
MPa
Flexural modulus (160°C)
4600
MPa
Flexural modulus (180°C)
4200
MPa
Flexural modulus (200°C)
3400
MPa
Flexural strength
330
MPa
Flexural strength (120°C)
115
MPa
Flexural strength (160°C)
100
MPa
Flexural strength (180°C)
90
MPa
Flexural strength (200°C)
75
MPa
Charpy impact strength (+23°C)
90
kJ/m²
Charpy impact strength (-30°C)
65
kJ/m²
Charpy notched impact strength (+23°C)
15
kJ/m²
Charpy notched impact strength (-30°C)
12
kJ/m²
Izod notched impact strength (+23°C)
15
kJ/m²

Thermal properties

Melting temperature (10°C/min)
282
°C
Glass transition temperature (10°C/min)
70
°C
Temp. of deflection under load (1.80 MPa)
256
°C
Temp. of deflection under load (0.45 MPa)
270
°C
Coeff. of linear therm. expansion (parallel)
0.25
E-4/°C
Coeff. of linear therm. expansion (normal)
0.5
E-4/°C

Electrical properties

Comparative tracking index
300
V

Other properties

Water absorption
6.7
%
Water absorption in water at 23°C after 24h
2.3
%
Humidity absorption
2.2
%
Density
1480
kg/m³

Material specific properties

Viscosity number
155
cm³/g

Rheological calculation properties

Density of melt
1320
kg/m³
Thermal conductivity of melt
0.314
W/(m K)
Spec. heat capacity melt
2130
J/(kg K)
Eff. thermal diffusivity
1.12E-7
m²/s

Diagrams

Applications

Charge Air Cooler Caps

Industry
Automotive
Material
  • •} Long term heat resistant
  • •} Lightweight
  • •} Cost effective
  • •} Fatigue resistant
}
More information

Hot Charged Air Ducts

Industry
Automotive
Material
  • •} Heat resistant
  • •} Lightweight
  • •} Reliable
  • •} Cost effective
}
More information

Integrated Air Inlet Manifolds (up to 230°C)

Industry
Automotive
Material
  • •} Long-term heat resistance up to 230 C
  • •} Lower system costs compared to metal.
}
More information