Pocan® BF4232HR 901510
30% Glass Reinforced, Injection Molding, Flame Retardant, Hydrolysis resistant
General Information
Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
Special features
- Hydrolysis resistant or enhanced hydrolytic stability
General Document
Regulatory Affairs
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Conflict minerals declaration (EICC, GeSI)2024-03-21
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-03-27
Yellow Card
Processing technology
Injection Molding
Injection Molding
Rheological properties
Melt volume-flow rate
16
cm³/10min
ISO 1133
Temperature
260
°C
ISO 1133
Load
2.16
kg
ISO 1133
Molding shrinkage (parallel)
0.4
%
ISO 294-4
Molding shrinkage (normal)
1.1
%
ISO 294-4
Mechanical properties
Tensile modulus
9800
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
12200
MPa
ISO 527-1/-2
Tensile modulus (40°C)
9640
MPa
ISO 527-1/-2
Tensile modulus (100°C)
5240
MPa
ISO 527-1/-2
Tensile modulus (120°C)
4330
MPa
ISO 527-1/-2
Tensile modulus (140°C)
3340
MPa
ISO 527-1/-2
Tensile modulus (160°C)
2820
MPa
ISO 527-1/-2
Tensile modulus (180°C)
2420
MPa
ISO 527-1/-2
Tensile modulus (200°C)
1960
MPa
ISO 527-1/-2
Stress at break
120
MPa
ISO 527-1/-2
Strain at break
2
%
ISO 527-1/-2
Flexural modulus
10000
MPa
ISO 178
Flexural strength
185
MPa
ISO 178
Flexural strain at flexural strength
2.3
%
ISO 178-A
Charpy impact strength (+23°C)
40
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
<10
kJ/m²
ISO 179/1eA
Izod impact strength (+23°C)
35
kJ/m²
ISO 180/1U
Thermal properties
Melting temperature (10°C/min)
225
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
195
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
215
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.3
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
1
E-4/°C
ISO 11359-1/-2
Burning Behav. at 1.5 mm nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Oxygen index
36.4
%
ISO 4589-1/-2
Ball pressure temperature
212
°C
IEC 60695-10-2
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
0.4
mm
IEC 60695-2-12
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (2) tested)
0.75
mm
IEC 60695-2-12
Glow Wire Ignition Temperature GWIT
900
°C
IEC 60695-2-13
GWIT (Thickness (1) tested)
0.4
mm
IEC 60695-2-13
Glow Wire Ignition Temperature GWIT
850
°C
IEC 60695-2-13
GWIT (Thickness (2) tested)
0.75
mm
IEC 60695-2-13
Glow Wire Ignition Temperature GWIT
725
°C
IEC 60695-2-13
GWIT (Thickness (3) tested)
1.5
mm
IEC 60695-2-13
Glow Wire Ignition Temperature GWIT
725
°C
IEC 60695-2-13
GWIT (Thickness (4) tested)
3
mm
IEC 60695-2-13
Electrical properties
Electric strength
29.8
kV/mm
IEC 60243-1
Comparative tracking index
225
V
IEC 60112
Comparative tracking index (PLC)
3
class
UL 746A
Other properties
Density
1670
kg/m³
ISO 1183