Pocan® B4225 000000
20% Glass Reinforced, Injection Molding, Flame Retardant
General Information
Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
Special features
General Document
Regulatory Affairs
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Conflict minerals declaration (EICC, GeSI)2024-03-21
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-03-27
Yellow Card
Processing technology
Injection Molding
Injection Molding
Rheological properties
Melt volume-flow rate
18
cm³/10min
ISO 1133
Temperature
260
°C
ISO 1133
Load
2.16
kg
ISO 1133
Molding shrinkage (parallel)
0.5
%
ISO 294-4
Molding shrinkage (normal)
1.2
%
ISO 294-4
Mechanical properties
Tensile modulus
7500
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
8550
MPa
ISO 527-1/-2
Tensile modulus (40°C)
6850
MPa
ISO 527-1/-2
Tensile modulus (100°C)
3620
MPa
ISO 527-1/-2
Tensile modulus (120°C)
3200
MPa
ISO 527-1/-2
Tensile modulus (140°C)
2620
MPa
ISO 527-1/-2
Tensile modulus (160°C)
2460
MPa
ISO 527-1/-2
Tensile modulus (180°C)
2080
MPa
ISO 527-1/-2
Tensile modulus (200°C)
1750
MPa
ISO 527-1/-2
Stress at break
125
MPa
ISO 527-1/-2
Strain at break
2.8
%
ISO 527-1/-2
Tensile creep modulus (1h)
7300
MPa
ISO 899-1
Tensile creep modulus (1000h)
6900
MPa
ISO 899-1
Flexural modulus
7200
MPa
ISO 178
Flexural strength
185
MPa
ISO 178
Flexural strain at flexural strength
3.2
%
ISO 178-A
Charpy impact strength (+23°C)
45
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
40
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
<10
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
<10
kJ/m²
ISO 179/1eA
Izod impact strength (+23°C)
40
kJ/m²
ISO 180/1U
Izod impact strength (-30°C)
35
kJ/m²
ISO 180-1U
Puncture - maximum force (+23°C)
628
N
ISO 6603-2
Puncture energy (+23°C)
1.8
J
ISO 6603-2
Thermal properties
Melting temperature (10°C/min)
225
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
200
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
220
°C
ISO 75-1/-2
Temp. of deflection under load (8.00 MPa)
126
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.3
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
1
E-4/°C
ISO 11359-1/-2
Burning Behav. at 1.5 mm nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
5VA
mm
IEC 60695-11-10
Burning Behav. 5V at thickness h
5VA
class
IEC 60695-11-20
Thickness tested
3.5
mm
IEC 60695-11-20
Oxygen index
32
%
ISO 4589-1/-2
Ball pressure temperature
215
°C
IEC 60695-10-2
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
0.75
mm
IEC 60695-2-12
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (2) tested)
1.5
mm
IEC 60695-2-12
Glow Wire Ignition Temperature GWIT
700
°C
IEC 60695-2-13
GWIT (Thickness (1) tested)
0.75
mm
IEC 60695-2-13
Glow Wire Ignition Temperature GWIT
700
°C
IEC 60695-2-13
GWIT (Thickness (2) tested)
1.5
mm
IEC 60695-2-13
Glow Wire Ignition Temperature GWIT
700
°C
IEC 60695-2-13
GWIT (Thickness (3) tested)
3
mm
IEC 60695-2-13
Electrical properties
Relative permittivity (100Hz)
3.8
-
IEC 62631-2-1
Relative permittivity (1 MHz)
3.6
-
IEC 62631-2-1
Dissipation factor (100 Hz)
40
E-4
IEC 62631-2-1
Dissipation factor (1 MHz)
180
E-4
IEC 62631-2-1
Volume resistivity
>1E13
Ohm*m
IEC 62631-3-1
Surface resistivity
>1E15
Ohm
IEC 62631-3-2
Electric strength
29
kV/mm
IEC 60243-1
Comparative tracking index
200
V
IEC 60112
Other properties
Water absorption
0.3
%
Sim. to ISO 62
Humidity absorption
0.1
%
Sim. to ISO 62
Density
1570
kg/m³
ISO 1183
Material specific properties
Viscosity number
97
cm³/g
ISO 307, 1157, 1628