Pocan® B3233HR 000000
30% Glass Reinforced, Injection Molding, Hydrolysis resistant, Improved flow
General Information
Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
Special features
- Good or high flow
- Hydrolysis resistant or enhanced hydrolytic stability
General Document
Regulatory Affairs
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Conflict minerals declaration (EICC, GeSI)2024-03-21
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-03-27
Yellow Card
Processing technology
Injection Molding
Injection Molding
Rheological properties
Melt volume-flow rate
15
cm³/10min
ISO 1133
Temperature
260
°C
ISO 1133
Load
2.16
kg
ISO 1133
Molding shrinkage (parallel)
0.3
%
ISO 294-4
Molding shrinkage (normal)
1
%
ISO 294-4
Mechanical properties
Tensile modulus
9600
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
9750
MPa
ISO 527-1/-2
Tensile modulus (40°C)
7180
MPa
ISO 527-1/-2
Tensile modulus (100°C)
3980
MPa
ISO 527-1/-2
Tensile modulus (120°C)
3540
MPa
ISO 527-1/-2
Tensile modulus (140°C)
3150
MPa
ISO 527-1/-2
Tensile modulus (160°C)
2840
MPa
ISO 527-1/-2
Tensile modulus (180°C)
2440
MPa
ISO 527-1/-2
Tensile modulus (200°C)
2010
MPa
ISO 527-1/-2
Stress at break
125
MPa
ISO 527-1/-2
Strain at break
2.9
%
ISO 527-1/-2
Flexural modulus
9100
MPa
ISO 178
Flexural strength
200
MPa
ISO 178
Flexural strain at flexural strength
3.2
%
ISO 178-A
Charpy impact strength (+23°C)
65
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
55
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
<10
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
<10
kJ/m²
ISO 179/1eA
Izod impact strength (+23°C)
55
kJ/m²
ISO 180/1U
Izod impact strength (-30°C)
55
kJ/m²
ISO 180-1U
Thermal properties
Melting temperature (10°C/min)
225
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
205
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
220
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.3
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
1.3
E-4/°C
ISO 11359-1/-2
Burning Behav. at 1.5 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Burning Behav. at 0.75 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
0.75
mm
IEC 60695-11-10
Ball pressure temperature
209
°C
IEC 60695-10-2
Glow Wire Flammability Index GWFI
800
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
0.8
mm
IEC 60695-2-12
Glow Wire Flammability Index GWFI
800
°C
IEC 60695-2-12
GWFI (Thickness (2) tested)
1.5
mm
IEC 60695-2-12
Glow Wire Ignition Temperature GWIT
825
°C
IEC 60695-2-13
GWIT (Thickness (1) tested)
0.8
mm
IEC 60695-2-13
Glow Wire Ignition Temperature GWIT
825
°C
IEC 60695-2-13
GWIT (Thickness (2) tested)
1.5
mm
IEC 60695-2-13
Glow Wire Ignition Temperature GWIT
825
°C
IEC 60695-2-13
GWIT (Thickness (3) tested)
3
mm
IEC 60695-2-13
Electrical properties
Volume resistivity
>1E13
Ohm*m
IEC 62631-3-1
Surface resistivity
>1E15
Ohm
IEC 62631-3-2
Electric strength
35
kV/mm
IEC 60243-1
Comparative tracking index
475
V
IEC 60112
Other properties
Density
1480
kg/m³
ISO 1183