Pocan® AF4110 000000
12% Glass Reinforced, Injection Molding, Flame Retardant, Low Warpage
General Information
Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
Special features
- Low warpage
General Document
Regulatory Affairs
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Conflict minerals declaration (EICC, GeSI)2024-03-21
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-03-27
Yellow Card
Processing technology
Injection Molding
Injection Molding
Rheological properties
Melt volume-flow rate
35
cm³/10min
ISO 1133
Temperature
260
°C
ISO 1133
Load
5
kg
ISO 1133
Molding shrinkage (parallel)
0.9
%
ISO 294-4
Molding shrinkage (normal)
0.8
%
ISO 294-4
Mechanical properties
Tensile modulus
5800
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
5820
MPa
ISO 527-1/-2
Tensile modulus (40°C)
4350
MPa
ISO 527-1/-2
Tensile modulus (100°C)
2520
MPa
ISO 527-1/-2
Tensile modulus (120°C)
1390
MPa
ISO 527-1/-2
Tensile modulus (140°C)
1040
MPa
ISO 527-1/-2
Tensile modulus (160°C)
669
MPa
ISO 527-1/-2
Tensile modulus (180°C)
420
MPa
ISO 527-1/-2
Stress at break
85
MPa
ISO 527-1/-2
Strain at break
2.5
%
ISO 527-1/-2
Flexural modulus
5500
MPa
ISO 178
Flexural strength
135
MPa
ISO 178
Flexural strain at flexural strength
2.8
%
ISO 178-A
Charpy impact strength (+23°C)
35
kJ/m²
ISO 179/1eU
Izod impact strength (+23°C)
30
kJ/m²
ISO 180/1U
Thermal properties
Melting temperature (10°C/min)
225
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
130
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
204
°C
ISO 75-1/-2
Burning Behav. at 1.5 mm nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Burning Behav. at 0.75 mm nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
0.75
mm
IEC 60695-11-10
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
0.75
mm
IEC 60695-2-12
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (2) tested)
1.5
mm
IEC 60695-2-12
Glow Wire Ignition Temperature GWIT
725
°C
IEC 60695-2-13
GWIT (Thickness (1) tested)
0.75
mm
IEC 60695-2-13
Glow Wire Ignition Temperature GWIT
700
°C
IEC 60695-2-13
GWIT (Thickness (2) tested)
1.5
mm
IEC 60695-2-13
Glow Wire Ignition Temperature GWIT
700
°C
IEC 60695-2-13
GWIT (Thickness (3) tested)
3
mm
IEC 60695-2-13
Electrical properties
Comparative tracking index
250
V
IEC 60112
Other properties
Density
1480
kg/m³
ISO 1183