Pocan® ECOT3230

30% Glass Reinforced, Injection Molding, Excellent Surface Properties, Recycled Content

Back to results

General Information

Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
Sustainability
Mass balanced, Recycled based
Special features
  • Contains recycled content
  • Good surface properties
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Compliance Statement EU Sanctions and Embargos2024-05-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Have a question? Contact us

Rheological properties

Melt volume-flow rate
30
cm³/10min
Temperature
260
°C
Load
5
kg
Molding shrinkage (parallel)
0.3
%
Molding shrinkage (normal)
0.9
%

Mechanical properties

Tensile modulus
10400
MPa
Stress at break
145
MPa
Strain at break
2.8
%
Flexural modulus
10300
MPa
Flexural strength
230
MPa
Flexural strain at flexural strength
3
%
Charpy impact strength (+23°C)
65
kJ/m²
Charpy impact strength (-30°C)
55
kJ/m²
Charpy notched impact strength (+23°C)
6.7
kJ/m²
Charpy notched impact strength (-30°C)
6.7
kJ/m²
Izod impact strength (+23°C)
55
kJ/m²
Izod impact strength (-30°C)
55
kJ/m²

Thermal properties

Temp. of deflection under load (1.80 MPa)
200
°C
Temp. of deflection under load (0.45 MPa)
220
°C
Coeff. of linear therm. expansion (parallel)
0.3
E-4/°C
Coeff. of linear therm. expansion (normal)
0.9
E-4/°C
Burning Behav. at 0.75 mm nom. thickn.
HB
class
Thickness tested
0.75
mm
Burning Behav. at 1.5 mm nom. thickn.
HB
class
Thickness tested
1.5
mm
UL recognition
Yes
-
Burning Behav. at 3.0 mm nom. thickn.
HB
class
Thickness tested
3
mm
UL recognition
Yes
-
Relative Temperature Index - electrical
140
°C
RTI electrical (Thickness (1) tested)
1
mm
Relative Temperature Index - with impact
120
°C
RTI with impact (Thickness (1) tested)
0.75
mm
Relative Temperature Index - with impact
125
°C
RTI with impact (Thickness (2) tested)
1.5
mm
Relative Temperature Index - without impact
140
°C
RTI without impact (Thickness (1) tested)
0.75
mm

Electrical properties

Comparative tracking index
250
V

Other properties

Water absorption
0.3
%
Humidity absorption
0.1
%
Density
1550
kg/m³

Material specific properties

Drying temperature circulating air dryer
120
°C
Drying time circulating air dryer
4-8
h
Residual moisture content
0.00-0.02
%
Melt temperature (Tmin - Tmax)
260-280
°C
Mold temperature
80-100
°C