Pocan® C5210
15% Mineral Reinforced, Injection Molding, Improved Impact, Excellent Surface Properties, Low Warpage
General Information
Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
Special features
- Good surface properties
- Low warpage
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Compliance Statement EU Sanctions and Embargos2024-05-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Processing technology
Injection Molding
Injection Molding
Rheological properties
Melt volume-flow rate
20
cm³/10min
ISO 1133
Temperature
270
°C
ISO 1133
Load
5
kg
ISO 1133
Molding shrinkage (parallel)
0.6
%
ISO 294-4
Molding shrinkage (normal)
0.6
%
ISO 294-4
Mechanical properties
Tensile modulus
3500
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
3770
MPa
ISO 527-1/-2
Tensile modulus (40°C)
3380
MPa
ISO 527-1/-2
Tensile modulus (100°C)
1820
MPa
ISO 527-1/-2
Tensile modulus (120°C)
1480
MPa
ISO 527-1/-2
Tensile modulus (140°C)
745
MPa
ISO 527-1/-2
Stress at break
45
MPa
ISO 527-1/-2
Strain at break
15
%
ISO 527-1/-2
Flexural modulus
3800
MPa
ISO 178
Flexural strength
85
MPa
ISO 178
Flexural strain at flexural strength
5
%
ISO 178-A
Charpy impact strength (+23°C)
N
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
N
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
12
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
7
kJ/m²
ISO 179/1eA
Izod impact strength (+23°C)
N
kJ/m²
ISO 180/1U
Izod impact strength (-30°C)
N
kJ/m²
ISO 180-1U
Puncture energy (+23°C)
35
J
ISO 6603-2
Thermal properties
Melting temperature (10°C/min)
250
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
105
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
125
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.5
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
0.8
E-4/°C
ISO 11359-1/-2
Burning Behav. at 0.75 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
0.75
mm
IEC 60695-11-10
Burning Behav. at 1.5 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Electrical properties
Comparative tracking index
225
V
IEC 60112
Other properties
Density
1300
kg/m³
ISO 1183
Material specific properties
Drying temperature circulating air dryer
120
°C
Drying time circulating air dryer
4-8
h
Residual moisture content
0.00-0.02
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
260-280
°C
Mold temperature
80-100
°C
admissible residence time at Tmax
<10
min