Pocan® BFN6410
17% White Pigments, Injection Molding, Flame Retardant (halogen free), Low Warpage
General Information
Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
Special features
- Low warpage
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Compliance Statement EU Sanctions and Embargos2024-05-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Injection Molding
Rheological properties
Molding shrinkage (parallel)
2.2
%
ISO 294-4
Molding shrinkage (normal)
2
%
ISO 294-4
Mechanical properties
Tensile modulus
4150
MPa
ISO 527-1/-2
Stress at break
40
MPa
ISO 527-1/-2
Strain at break
1.8
%
ISO 527-1/-2
Flexural modulus
4200
MPa
ISO 178
Flexural strength
70
MPa
ISO 178
Flexural strain at flexural strength
2.3
%
ISO 178-A
Charpy impact strength (+23°C)
17
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
17
kJ/m²
ISO 179/1eU
Izod impact strength (+23°C)
15
kJ/m²
ISO 180/1U
Thermal properties
Melting temperature (10°C/min)
220
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
100
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
180
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.8
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
0.9
E-4/°C
ISO 11359-1/-2
Burning Behav. at 0.75 mm nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
0.75
mm
IEC 60695-11-10
Burning Behav. at 1.5 mm nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
UL recognition
Yes
-
-
Burning Behav. at 3.0 mm nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
3
mm
IEC 60695-11-10
UL recognition
Yes
-
-
Burning Behav. 5V at thickness h
5VB
class
IEC 60695-11-20
Thickness tested
1.5
mm
IEC 60695-11-20
UL recognition
Yes
-
-
Oxygen index
41
%
ISO 4589-1/-2
Ball pressure temperature
205
°C
IEC 60695-10-2
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
0.4
mm
IEC 60695-2-12
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (2) tested)
0.75
mm
IEC 60695-2-12
Electrical properties
Electric strength
28
kV/mm
IEC 60243-1
Comparative tracking index
400
V
IEC 60112
Comparative tracking index (PLC)
1
class
UL 746A
Other properties
Water absorption
0.4
%
Sim. to ISO 62
Humidity absorption
0.2
%
Sim. to ISO 62
Density
1520
kg/m³
ISO 1183
Material specific properties
Drying temperature circulating air dryer
120
°C
Drying time circulating air dryer
4-8
h
Residual moisture content
0.00-0.02
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
250-265
°C
Mold temperature
70-90
°C
admissible residence time at Tmax
<5
min