Pocan® BF2505

Unreinforced, Injection Molding, Flame Retardant

Back to results

General Information

Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
Special features
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Compliance Statement EU Sanctions and Embargos2024-05-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
2.2
%
Molding shrinkage (normal)
2.2
%

Mechanical properties

Tensile modulus
3000
MPa
Yield stress
50
MPa
Yield strain
3
%
Nominal strain at break
8
%
Flexural modulus
3000
MPa
Flexural strength
90
MPa
Flexural strain at flexural strength
5.5
%
Izod impact strength (+23°C)
100
kJ/m²

Thermal properties

Melting temperature (10°C/min)
225
°C
Temp. of deflection under load (1.80 MPa)
60
°C
Burning Behav. at 0.75 mm nom. thickn.
V-0
class
Thickness tested
0.75
mm
Burning Behav. at 1.5 mm nom. thickn.
V-0
class
Thickness tested
1.5
mm
UL recognition
Yes
-
Burning Behav. at 3.0 mm nom. thickn.
V-0
class
Thickness tested
3
mm
UL recognition
Yes
-
Glow Wire Flammability Index GWFI
960
°C
GWFI (Thickness (1) tested)
0.75
mm
Glow Wire Ignition Temperature GWIT
875
°C
GWIT (Thickness (1) tested)
0.75
mm
Relative Temperature Index - electrical
130
°C
RTI electrical (Thickness (1) tested)
0.75
mm
Relative Temperature Index - with impact
120
°C
RTI with impact (Thickness (1) tested)
0.75
mm
Relative Temperature Index - with impact
130
°C
RTI with impact (Thickness (2) tested)
1.5
mm
Relative Temperature Index - without impact
140
°C
RTI without impact (Thickness (1) tested)
0.75
mm

Electrical properties

Comparative tracking index (PLC)
0
class

Other properties

Density
1430
kg/m³

Material specific properties

Drying temperature circulating air dryer
120
°C
Drying time circulating air dryer
4-8
h
Residual moisture content
0.00-0.02
%
Melt temperature (Tmin - Tmax)
240-260
°C
Mold temperature
80-100
°C