Pocan® B4235Z

30% Glass Reinforced, Injection Molding, Flame Retardant, Improved Impact

Back to results

General Information

Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
Special features
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-09-12
  • 2024-05-16
Yellow Card
Processing technology
Injection Molding
Have a question? Contact us

Rheological properties

Melt volume-flow rate
26
cm³/10min
Temperature
260
°C
Load
5
kg
Molding shrinkage (parallel)
0.3
%
Molding shrinkage (normal)
0.9
%

Mechanical properties

Tensile modulus
10000
MPa
Stress at break
125
MPa
Strain at break
2.8
%
Flexural modulus
9700
MPa
Flexural strength
210
MPa
Flexural strain at flexural strength
3.2
%
Charpy impact strength (+23°C)
60
kJ/m²
Charpy impact strength (-30°C)
60
kJ/m²
Charpy notched impact strength (+23°C)
<10
kJ/m²
Charpy notched impact strength (-30°C)
<10
kJ/m²
Izod impact strength (+23°C)
55
kJ/m²
Izod impact strength (-30°C)
55
kJ/m²

Thermal properties

Melting temperature (10°C/min)
225
°C
Temp. of deflection under load (1.80 MPa)
200
°C
Temp. of deflection under load (0.45 MPa)
220
°C
Temp. of deflection under load (8.00 MPa)
130
°C
Coeff. of linear therm. expansion (parallel)
0.2
E-4/°C
Coeff. of linear therm. expansion (normal)
1
E-4/°C
Burning Behav. at 0.75 mm nom. thickn.
V-2
class
Thickness tested
0.75
mm
Burning Behav. at 1.5 mm nom. thickn.
V-0
class
Thickness tested
1.5
mm
UL recognition
Yes
-
Burning Behav. at 3.0 mm nom. thickn.
V-0
class
Thickness tested
3
mm
UL recognition
Yes
-
Burning Behav. 5V at thickness h
5VA
class
Thickness tested
3
mm
UL recognition
Yes
-
Ball pressure temperature
210
°C
Glow Wire Flammability Index GWFI
960
°C
GWFI (Thickness (1) tested)
2
mm
Relative Temperature Index - electrical
130
°C
RTI electrical (Thickness (1) tested)
0.75
mm
Relative Temperature Index - with impact
130
°C
RTI with impact (Thickness (1) tested)
0.75
mm
Relative Temperature Index - without impact
140
°C
RTI without impact (Thickness (1) tested)
0.75
mm

Electrical properties

Comparative tracking index
175
V
Comparative tracking index (PLC)
3
class

Other properties

Water absorption
0.4
%
Humidity absorption
0.1
%
Density
1620
kg/m³

Material specific properties

Viscosity number
83
cm³/g
Drying temperature circulating air dryer
120
°C
Drying time circulating air dryer
4-8
h
Residual moisture content
0.00-0.02
%
Melt temperature (Tmin - Tmax)
240-260
°C
Mold temperature
80-100
°C

JSON SPT

Melt volume-flow rate
26
cm³/10min
Temperature
260
°C
Load
5
kg
Molding shrinkage (parallel)
0.3
%
Molding shrinkage (normal)
0.9
%