Pocan® B3225XF

20% Glass Fiber Reinforced, Injection Molding, High Flow, Impact Modified

Back to results

General Information

Pocan® is a high-quality brand of polybutylene terephthalate (PBT) and PBT blends crafted by Envalior. Pocan is known for its impressive resistance to heat and chemicals, outstanding electrical properties, strength and hardness. It is designed to cater to a wide range of industries, including automotive, electrical/electronics, lighting, household appliances, and sports & leisure.
Special features
  • Good or high flow
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2025-11-21
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals and F-gasses2025-02-06
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2025-04-14
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration POPs (Persistent Organic Pollutants)2025-10-21
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Compliance Statement Sanctions and Embargos2025-11-24
  • Conflict minerals declaration (EICC, GeSI)2025-10-21
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2025-11-03
  • EMRT Statement2025-05-27
  • Micro Plastics Statement2025-09-22
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • Packaging, Packaging Waste (EU) 2025/40 and CONEG declaration2025-06-24
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2025-11-06
Yellow Card
Processing technology
Injection Molding
Automotive OEM
GM
OEM Specification
GMW16733
Have a question? Contact us

Rheological properties

Melt volume-flow rate
35
cm³/10min
Temperature
260
°C
Load
2.16
kg
Molding shrinkage (parallel)
0.5
%
Molding shrinkage (normal)
1.1
%

Mechanical properties

Tensile modulus
6500
MPa
Tensile modulus (-40°C)
7380
MPa
Tensile modulus (40°C)
5090
MPa
Tensile modulus (100°C)
3050
MPa
Tensile modulus (120°C)
2760
MPa
Tensile modulus (140°C)
2470
MPa
Tensile modulus (160°C)
2190
MPa
Tensile modulus (180°C)
1840
MPa
Tensile modulus (200°C)
1260
MPa
Stress at break
105
MPa
Strain at break
3.5
%
Flexural modulus
6100
MPa
Flexural strength
165
MPa
Flexural strain at flexural strength
3.7
%
Charpy impact strength (+23°C)
60
kJ/m²
Charpy impact strength (-30°C)
40
kJ/m²
Charpy notched impact strength (+23°C)
8.3
kJ/m²
Charpy notched impact strength (-30°C)
7.2
kJ/m²
Izod impact strength (+23°C)
50
kJ/m²
Izod impact strength (-30°C)
40
kJ/m²

Thermal properties

Melting temperature (10°C/min)
225
°C
Temp. of deflection under load (1.80 MPa)
200
°C
Temp. of deflection under load (0.45 MPa)
220
°C
Temp. of deflection under load (8.00 MPa)
130
°C
Coeff. of linear therm. expansion (parallel)
0.2
E-4/°C
Coeff. of linear therm. expansion (normal)
1.3
E-4/°C
Burning Behav. at 0.75 mm nom. thickn.
HB
class
Thickness tested
0.75
mm
Burning Behav. at 1.5 mm nom. thickn.
HB
class
Thickness tested
1.5
mm
UL recognition
Yes
-
Burning Behav. at 3.0 mm nom. thickn.
HB
class
Thickness tested
3
mm
UL recognition
Yes
-
Glow Wire Flammability Index GWFI
750
°C
GWFI (Thickness (1) tested)
2
mm
Glow Wire Ignition Temperature GWIT
775
°C
GWIT (Thickness (1) tested)
2
mm

Electrical properties

Comparative tracking index
400
V

Other properties

Water absorption
0.4
%
Humidity absorption
0.1
%
Density
1400
kg/m³

Material specific properties

Drying temperature circulating air dryer
120
°C
Drying time circulating air dryer
4-8
h
Residual moisture content
0.00-0.02
%
Melt temperature (Tmin - Tmax)
250-270
°C
Mold temperature
80-100
°C