Novamid® 1010GN8-30 NAT

30% Glass Reinforced, Flame Retardant, Halogen free

Back to results

General Information

Novamid® is a high-quality polyamide, that has been developed as a special product line in order to cope with high demand levels from our Japanese customers.
Novamid® has seen various applications in various fields and various regions. From car to packaging, Novamid® is supported by an experienced and wide range of experts.
Special features
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-04-25
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
  • Absence Declaration Red Phosphorus2023-11-16
  • Conflict minerals declaration (EICC, GeSI)2024-03-21
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
  • Turkish customs legislation info letter (EK-8 form)2023-11-16
Yellow Card
Processing technology
Injection Molding
Have a question? Contact us

Rheological properties

Melt volume-flow rate
10
cm³/10min
Temperature
270
°C
Load
5
kg
Melt flow index MFI
13
g/10min
MFI test temperature
270
°C
MFI test load
5
kg
Molding shrinkage (parallel)
0.3
%
Molding shrinkage (normal)
0.8
%

Mechanical properties

Tensile modulus
12000
MPa
Stress at break
140
MPa
Strain at break
2.5
%
Flexural modulus
10200
MPa
Flexural strength
220
MPa
Charpy impact strength (+23°C)
63
kJ/m²
Charpy notched impact strength (+23°C)
10
kJ/m²

Thermal properties

Melting temperature (10°C/min)
220
°C
Temp. of deflection under load (1.80 MPa)
210
°C
Temp. of deflection under load (0.45 MPa)
220
°C
Relative Temperature Index - electrical
65
°C
RTI electrical (Thickness (1) tested)
0.75
mm
Relative Temperature Index - with impact
65
°C
RTI with impact (Thickness (1) tested)
0.75
mm
Relative Temperature Index - without impact
65
°C
RTI without impact (Thickness (1) tested)
0.75
mm

Electrical properties

Relative permittivity (1 MHz)
3.2
-
Dissipation factor (1 MHz)
200
E-4
Volume resistivity
1E13
Ohm*m
Surface resistivity
Ohm
Electric strength
23
kV/mm
Comparative tracking index
600
V

Other properties

Humidity absorption
1.3
%
Density
1430
kg/m³