Novamid® 1013C5

Injection Molding, Molding Release, Improved Processing, Lubricated, Nucleated

Back to results

General Information

Novamid® is a high-quality polyamide, that has been developed as a special product line in order to cope with high demand levels from our Japanese customers.
Novamid® has seen various applications in various fields and various regions. From car to packaging, Novamid® is supported by an experienced and wide range of experts.
Product
Good and fast flow-ability. Very easy mold release. Medium viscosity in injection molding grades. Ideal for high cycle injection molding production.
Special features
  • Contains release agent
  • Lubricated
  • Nucleated
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Absence Declaration Red Phosphorus2023-11-16
  • Compliance Statement EU Sanctions and Embargos2024-05-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Have a question? Contact us

Rheological properties

Melt volume-flow rate
34
cm³/10min
Temperature
230
°C
Load
2.16
kg
Melt flow index MFI
34
g/10min
MFI test temperature
230
°C
MFI test load
2.16
kg
Molding shrinkage [parallel]
1.2
%
Molding shrinkage [normal]
1.3
%

Mechanical properties

Tensile modulus
3100
MPa
Yield stress
82
MPa
Nominal strain at break
18
%
Flexural modulus
2800
MPa
Flexural strength
110
MPa
Charpy impact strength (+23°C)
N
kJ/m²
Charpy notched impact strength (+23°C)
3
kJ/m²

Thermal properties

Melting temperature (10°C/min)
220
°C
Temp. of deflection under load (1.80 MPa)
75
°C
Temp. of deflection under load (0.45 MPa)
169
°C
Burning Behav. at 1.5 mm nom. thickn.
V-2
class
Thickness tested
1.5
mm
UL recognition
Yes
-
Burning Behav. at 3.0 mm nom. thickn.
V-2
class
Thickness tested
V-2
mm
UL recognition
3
-
Relative Temperature Index - electrical
130
°C
RTI electrical (Thickness (1) tested)
0.81
mm
Relative Temperature Index - electrical
130
°C
RTI electrical (Thickness (2) tested)
3
mm
Relative Temperature Index - with impact
65
°C
RTI with impact (Thickness (1) tested)
0.81
mm
Relative Temperature Index - with impact
75
°C
RTI with impact (Thickness (2) tested)
3
mm
Relative Temperature Index - without impact
80
°C
RTI without impact (Thickness (1) tested)
0.81
mm
Relative Temperature Index - without impact
85
°C
RTI without impact (Thickness (2) tested)
3
mm

Electrical properties

Relative permittivity (100Hz)
4
-
Relative permittivity (1 MHz)
4
-
Dissipation factor (100 Hz)
110
E-4
Dissipation factor (1 MHz)
220
E-4
Volume resistivity
>1E13
Ohm*m
Surface resistivity
Ohm
Electric strength
26
kV/mm
Comparative tracking index
600
V

Other properties

Humidity absorption
2.8
%
Density
1130
kg/m³

Material specific properties

Viscosity number
133
cm³/g