Mechanical properties
Tensile modulus
2850
MPa
ISO 527-1/-2
Yield stress
80
MPa
ISO 527-1/-2
Flexural modulus
2600
MPa
ISO 178
Flexural strength
90
MPa
ISO 178
Charpy impact strength (+23°C)
N
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
5
kJ/m²
ISO 179/1eA
Thermal properties
Melting temperature (10°C/min)
220
°C
ISO 11357-1/-3
Coeff. of linear therm. expansion (parallel)
0.9
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
1
E-4/°C
ISO 11359-1/-2
Other properties
Water absorption
9.5
%
Sim. to ISO 62
Humidity absorption
2.5
%
Sim. to ISO 62
Density
1130
kg/m³
ISO 1183
Material specific properties
Viscosity number
168
cm³/g
ISO 307, 1157, 1628
RSV formic acid, 1g/100ml
2.7
-
Envalior Method
Melt Viscosity (260 °C)
410
Pa s
Envalior Method, 260 °C
Rheological calculation properties
Spec. heat capacity
1550
J/(kg K)
-
Average spec. heat capacity 20-150 °C
2250
J/(kg K)
Mechanical properties (Film)
Modulus of elasticity
460
MPa
Envalior Method, 50 mm/min
Stress at yield, parallel
32
MPa
ISO 527-3
Maximum stress, parallel
80
MPa
ISO 527-3
Maximum strain, parallel
350
%
ISO 527-3
Trouser Tear resistance, parallel
32
-
ISO 6383-1
Puncture resistance
1150
J/m
Envalior Method
Static coefficient of friction
1.5
-
ISO 8295
Dynamic coefficient of friction
1.2
-
ISO 8295
Other properties (Film)
Transparency/Clarity
83
%
Envalior Method
Oxygen transmission rate at 23°C/0%r.h.
26
cm³/(m²*d*bar)
DIS 15105-1/-2
Oxygen transmission rate at 23°C/85%r.h.
38
cm³/(m²*d*bar)
DIS 15105-1/-2
Water Vapor Transmission Rate at 23°C/85%r.h.
35
g/(m²*d)
DIS 15106-1/-3