ForTii® Ace MX54B
60% Glass Reinforced, PA4T, Heat Stabilized, for Structural Parts
General Information
ForTii® is a breakthrough high temperature polyamide with halogen-free and halogen containing flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries.
We developed ForTii® in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want – and need.
ForTii® Ace is a PPA with a high Glass Transition Temperature, with extreme chemical resistance, suitable for applications that need high mechanics at elevated temperatures.
Product
ForTii® Ace MX54B is a high Tg PPA combining good toughness at low temperatures and chemical resistance. It is designed to have a dimensional stability close to aluminum. It has a high mechanical performance over a broad temperature range, from -35°C to above 150°C, both in dry as well as conditioned environment.
ForTii® Ace MX54B is a high Tg PPA combining good toughness at low temperatures and chemical resistance. It is designed to have a dimensional stability close to aluminum. It has a high mechanical performance over a broad temperature range, from -35°C to above 150°C, both in dry as well as conditioned environment.
Special features
- Heat stabilized
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration Biocidal Products2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration EPA 20 High Priority Substances 20192023-11-16
- Absence Declaration Food Allergens2023-11-16
- Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-04-25
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration PFAS2024-03-05
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-03-21
- Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
- REACH Registration Statement2024-03-27
- REACH STATEMENT KOREA2023-11-16
- REACH STATEMENT TURKYE2023-11-16
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-03-27
- Turkish customs legislation info letter (EK-8 form)2023-11-16
Processing technology
Injection Molding
Injection Molding
Applications
Rheological properties
Molding shrinkage (parallel)
0.4
%
ISO 294-4
Molding shrinkage (normal)
0.8
%
ISO 294-4
Spiral flow length 1.0 mm 1000 bar
66
mm
-
Spiral flow length 1.0 mm 1200 bar
77
mm
-
Mechanical properties
Tensile modulus
23000
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
25000
MPa
ISO 527-1/-2
Tensile modulus (40°C)
22500
MPa
ISO 527-1/-2
Tensile modulus (80°C)
22000
MPa
ISO 527-1/-2
Tensile modulus (100°C)
21500
MPa
ISO 527-1/-2
Tensile modulus (120°C)
20500
MPa
ISO 527-1/-2
Tensile modulus (150°C)
12500
MPa
ISO 527-1/-2
Tensile modulus (160°C)
9800
MPa
ISO 527-1/-2
Tensile modulus (180°C)
8100
MPa
ISO 527-1/-2
Tensile modulus (200°C)
7400
MPa
ISO 527-1/-2
Tensile modulus (210°C)
7000
MPa
ISO 527-1/-2
Stress at break
270
MPa
ISO 527-1/-2
Stress at break (-40°C)
330
MPa
ISO 527-1/-2
Stress at break (40°C)
260
MPa
ISO 527-1/-2
Stress at break (80°C)
230
MPa
ISO 527-1/-2
Stress at break (100°C)
210
MPa
ISO 527-1/-2
Stress at break (120°C)
180
MPa
ISO 527-1/-2
Stress at break (150°C)
115
MPa
ISO 527-1/-2
Stress at break (160°C)
95
MPa
ISO 527-1/-2
Stress at break (180°C)
75
MPa
ISO 527-1/-2
Stress at break (200°C)
65
MPa
ISO 527-1/-2
Stress at break (210°C)
60
MPa
ISO 527-1/-2
Strain at break
1.8
%
ISO 527-1/-2
Strain at break (-40°C)
1.8
%
ISO 527-1/-2
Strain at break (40°C)
1.75
%
ISO 527-1/-2
Strain at break (80°C)
1.8
%
ISO 527-1/-2
Strain at break (100°C)
1.8
%
ISO 527-1/-2
Strain at break (120°C)
1.9
%
ISO 527-1/-2
Strain at break (150°C)
3.5
%
ISO 527-1/-2
Strain at break (160°C)
4
%
ISO 527-1/-2
Strain at break (180°C)
4
%
ISO 527-1/-2
Strain at break (200°C)
4
%
ISO 527-1/-2
Strain at break (210°C)
4
%
ISO 527-1/-2
Flexural modulus
23500
MPa
ISO 178
Flexural modulus (120°C)
20000
MPa
ISO 178
Flexural modulus (160°C)
12000
MPa
ISO 178
Flexural modulus (180°C)
9000
MPa
ISO 178
Flexural modulus (200°C)
8200
MPa
ISO 178
Flexural modulus (210°C)
7900
MPa
ISO 178
Flexural strength
420
MPa
ISO 178
Flexural strength (120°C)
270
MPa
ISO 178
Flexural strength (160°C)
150
MPa
ISO 178
Flexural strength (180°C)
120
MPa
ISO 178
Flexural strength (200°C)
105
MPa
ISO 178
Flexural strength (210°C)
100
MPa
ISO 178
Charpy impact strength (+23°C)
90
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
75
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
13
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
13
kJ/m²
ISO 179/1eA
Weldline strength at thickness 1
95
MPa
ISO 527-1/-2
Weldline strain at thickness 1
0.7
%
ISO 527-1/-2
Thickness tested (1)
4
mm
ISO 527-1/-2
Thermal properties
Melting temperature (10°C/min)
330
°C
ISO 11357-1/-3
Glass Transition Temperature from DMTA (tan d)
155
°C
ASTM D5026/D7028
Temp. of deflection under load (1.80 MPa)
307
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
320
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.13
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
0.41
E-4/°C
ISO 11359-1/-2
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
3
mm
IEC 60695-2-12
Glow Wire Flammability Index GWFI
725
°C
IEC 60695-2-12
GWFI (Thickness (2) tested)
1.5
mm
IEC 60695-2-12
Glow Wire Ignition Temperature GWIT
850
°C
IEC 60695-2-13
GWIT (Thickness (1) tested)
3
mm
IEC 60695-2-13
Glow Wire Ignition Temperature GWIT
725
°C
IEC 60695-2-13
GWIT (Thickness (2) tested)
1.5
mm
IEC 60695-2-13
Thermal Index 2500 hrs
189
°C
IEC 60216/ISO 527-1/-2
Thermal Index 5000 hrs
176
°C
IEC 60216/ISO 527-1/-2
Thermal Index 10000 hrs
165
°C
IEC 60216/ISO 527-1/-2
Thermal Index 20000 hrs
153
°C
IEC 60216/ISO 527-1/-2
Electrical properties
Comparative tracking index
425
V
IEC 60112
Other properties
Water absorption
2.5
%
Sim. to ISO 62
Humidity absorption
1.2
%
Sim. to ISO 62
Density
1780
kg/m³
ISO 1183
Diagrams
Applications
Structural Parts with ForTii® Ace
Industry
Automotive
Material
ForTii® Ace is the game changer in metal replacement. With a Tg of 150-160°C, this material offers linear and stable strength and stiffness at elevated temperatures. Excellent chemical resistance versus coolants (water/glycol), road salt, acid, mineral oil, transmission oil, etc.}
Timing drive systems
Industry
Automotive
Material
For more than 20 years, Envalior has helped the world’s leading automakers improve the performance and efficiency of timing chain systems, wear guide faces, support arms, and related thermoplastic components through advanced material science.
Envalior offers a full portfolio of durable thermoplastic materials formulated to reduce timing chain friction and improve efficiency. To protect the environment and aid regulatory compliance, Envalior offers letters of conformity for any grades with PTFE confirming they do not contain harmful PFAS or PFOA.
In addition, Envalior offers superior PTFE-free solutions with best-in-class low-friction performance such as Stanyl® HGR3.}