Durethan® ECOBKV40H2.0
40% Glass Reinforced, Injection Molding, Heat Stabilized, Recycled Content
General Information
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Sustainability
Mass balanced, Recycled based
Mass balanced, Recycled based
Special features
- Contains recycled content
- Heat stabilized
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
Yellow Card
Processing technology
Injection Molding
Injection Molding
Mechanical properties
Tensile modulus
12700
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
13700
MPa
ISO 527-1/-2
Tensile modulus (40°C)
11200
MPa
ISO 527-1/-2
Tensile modulus (100°C)
5680
MPa
ISO 527-1/-2
Tensile modulus (120°C)
5330
MPa
ISO 527-1/-2
Tensile modulus (140°C)
5030
MPa
ISO 527-1/-2
Tensile modulus (160°C)
4730
MPa
ISO 527-1/-2
Tensile modulus (180°C)
4410
MPa
ISO 527-1/-2
Tensile modulus (200°C)
3860
MPa
ISO 527-1/-2
Stress at break
195
MPa
ISO 527-1/-2
Strain at break
3
%
ISO 527-1/-2
Flexural modulus
11200
MPa
ISO 178
Flexural strength
310
MPa
ISO 178
Charpy impact strength (+23°C)
95
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
85
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
15
kJ/m²
ISO 179/1eA
Izod notched impact strength (+23°C)
18
kJ/m²
ISO 180/1A
Thermal properties
Melting temperature (10°C/min)
222
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
200
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
215
°C
ISO 75-1/-2
Burning Behav. at 1.5 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Glow Wire Flammability Index GWFI
650
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
2
mm
IEC 60695-2-12
Electrical properties
Relative permittivity (100Hz)
4
-
IEC 62631-2-1
Relative permittivity (1 MHz)
4
-
IEC 62631-2-1
Dissipation factor (100 Hz)
50
E-4
IEC 62631-2-1
Dissipation factor (1 MHz)
150
E-4
IEC 62631-2-1
Volume resistivity
1E13
Ohm*m
IEC 62631-3-1
Surface resistivity
Ohm
IEC 62631-3-2
Electric strength
40
kV/mm
IEC 60243-1
Comparative tracking index
400
V
IEC 60112
Other properties
Water absorption
6
%
Sim. to ISO 62
Humidity absorption
1.8
%
Sim. to ISO 62
Density
1460
kg/m³
ISO 1183
Material specific properties
Viscosity number
140
cm³/g
ISO 307, 1157, 1628
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
270-290
°C
Mold temperature
80-120
°C